Influences of the tempering temperature on the microstructure, mechanical property and wear resistance of High-Boron High Speed Steel (HBHSS) roll materials were investigated by means of optical microscopy, scanning e...Influences of the tempering temperature on the microstructure, mechanical property and wear resistance of High-Boron High Speed Steel (HBHSS) roll materials were investigated by means of optical microscopy, scanning electron microscopy (SEM), X-ray diffraction, hardness measurement, impact tester, tensile tester and pin abrasion tester. The results show that the as-cast structure of HBHSS consists of a great amount of martensite and M2(B,C) and a few retained austenites and M23(B,C)6. After solution treated at 1,050 °C and followed by oil cooling, the amount of M23(B,C)6 carbo-borides in quenched HBHSS increases obviously and the macrohardness of the quenched HBHSS is 66 HRC, which is very close to the 65.8 HRC of as-cast HBHSS. On the whole, the hardness of HBHSS alloy shows a trend of slight decrease with increasing tempering temperature when tempered below 500 °C. While when above 500 °C, the hardness increases slightly as the tempering temperature increases and reaches a peak at 525 °C and then decreases obviously. The impact toughness of HBHSS has a tendency to increase as the tempering temperature increases. Tempering can improve the tensile strength and elongation of HBHSS, but a higher tempering temperature causes a slight decrease in both tensile strength and elongation. Excellent wear resistance can be obtained by tempering at 500 to 550 °C.展开更多
基金supported by the Scientific Plan Project of Beijing Education Committee (PXM2012- 014204-00-000136, PXM2012-014204-00-000156)the National Natural Science Foundation of China (Grant No. 51054008)Science and Technology Cooperating Project of Yunnan Province, China (Grant No.2010AD012)
文摘Influences of the tempering temperature on the microstructure, mechanical property and wear resistance of High-Boron High Speed Steel (HBHSS) roll materials were investigated by means of optical microscopy, scanning electron microscopy (SEM), X-ray diffraction, hardness measurement, impact tester, tensile tester and pin abrasion tester. The results show that the as-cast structure of HBHSS consists of a great amount of martensite and M2(B,C) and a few retained austenites and M23(B,C)6. After solution treated at 1,050 °C and followed by oil cooling, the amount of M23(B,C)6 carbo-borides in quenched HBHSS increases obviously and the macrohardness of the quenched HBHSS is 66 HRC, which is very close to the 65.8 HRC of as-cast HBHSS. On the whole, the hardness of HBHSS alloy shows a trend of slight decrease with increasing tempering temperature when tempered below 500 °C. While when above 500 °C, the hardness increases slightly as the tempering temperature increases and reaches a peak at 525 °C and then decreases obviously. The impact toughness of HBHSS has a tendency to increase as the tempering temperature increases. Tempering can improve the tensile strength and elongation of HBHSS, but a higher tempering temperature causes a slight decrease in both tensile strength and elongation. Excellent wear resistance can be obtained by tempering at 500 to 550 °C.