Infrared solar cells are more efective than normal bandgap solar cells at reducing the spectral loss in the near-infrared region,thus also at broadening the absorption spectra and improving power conversion efciency.P...Infrared solar cells are more efective than normal bandgap solar cells at reducing the spectral loss in the near-infrared region,thus also at broadening the absorption spectra and improving power conversion efciency.PbS colloidal quantum dots(QDs)with tunable bandgap are ideal infrared photovoltaic materials.However,QD solar cell production sufers from small-areabased spin-coating fabrication methods and unstable QD ink.Herein,the QD ink stability mechanism was fully investigated according to Lewis acid–base theory and colloid stability theory.We further studied a mixed solvent system using dimethylformamide and butylamine,compatible with the scalable manufacture of method-blade coating.Based on the ink system,100 cm2 of uniform and dense near-infrared PbS QDs(~0.96 eV)flm was successfully prepared by blade coating.The average efciencies of above absorber-based devices reached 11.14%under AM1.5G illumination,and the 800 nm-fltered efciency achieved 4.28%.Both were the top values among blade coating method based devices.The newly developed ink showed excellent stability,and the device performance based on the ink stored for 7 h was similar to that of fresh ink.The matched solvent system for stable PbS QD ink represents a crucial step toward large area blade coating photoelectric devices.展开更多
基金HS acknowledges the financial support from the National Natural Science Foundation of China(Grant No.62374065)the Interdisciplinary Research promotion of HUST(No.2023JCYJ040)+4 种基金the Innovation Project of Optics Valley Laboratory(No.OVL2021BG008)the Program of Science Technology of Wenzhou City(No.G20210011)HH acknowledges the fnancial support from the Innovation and Technology Commission(No.MHP/104/21)the Shenzhen Science Technology and Innovation Commission(No.JCYJ20210324125612035)the City University of Hong Kong(Nos.9360140,7005720,9667229,9680331,7005580,and 9678291)。
文摘Infrared solar cells are more efective than normal bandgap solar cells at reducing the spectral loss in the near-infrared region,thus also at broadening the absorption spectra and improving power conversion efciency.PbS colloidal quantum dots(QDs)with tunable bandgap are ideal infrared photovoltaic materials.However,QD solar cell production sufers from small-areabased spin-coating fabrication methods and unstable QD ink.Herein,the QD ink stability mechanism was fully investigated according to Lewis acid–base theory and colloid stability theory.We further studied a mixed solvent system using dimethylformamide and butylamine,compatible with the scalable manufacture of method-blade coating.Based on the ink system,100 cm2 of uniform and dense near-infrared PbS QDs(~0.96 eV)flm was successfully prepared by blade coating.The average efciencies of above absorber-based devices reached 11.14%under AM1.5G illumination,and the 800 nm-fltered efciency achieved 4.28%.Both were the top values among blade coating method based devices.The newly developed ink showed excellent stability,and the device performance based on the ink stored for 7 h was similar to that of fresh ink.The matched solvent system for stable PbS QD ink represents a crucial step toward large area blade coating photoelectric devices.
