A solid polymer electrolyte (SPE) films consist-ing of polyethylene oxide (PEO), 50% epoxi-dized natural rubber (ENR50) and LiCF3SO3 with various compositions of PEO-ENR50 and vari-ous weight percentage of LiCF3SO3 we...A solid polymer electrolyte (SPE) films consist-ing of polyethylene oxide (PEO), 50% epoxi-dized natural rubber (ENR50) and LiCF3SO3 with various compositions of PEO-ENR50 and vari-ous weight percentage of LiCF3SO3 were pre-pared by solution casting technique. The poly-mer electrolyte films were characterized using DSC, XRD and AC impedance spectroscopy. The SPE with the PEO-ENR50 composition of 70-30 shows the highest conductivity of 4.2 × 10-5 Scm-1 at the 15 wt.% of LiCF3SO3 compared with the other composition of PEO/ENR50. This composition was then chosen to investigate the effect of LiCF3SO3 on the thermal property, structure and conductivity of the electrolyte. The highest room temperature conductivity of 1.4 × 10-4 Scm-1 was achieved at 20 wt.% of LiCF3SO3. The conductivity result is supported by the DSC and XRD analysis which showed the semi- crystalline nature of PEO turning to amor-phous state due to the increase in LiCF3SO3 content.展开更多
文摘A solid polymer electrolyte (SPE) films consist-ing of polyethylene oxide (PEO), 50% epoxi-dized natural rubber (ENR50) and LiCF3SO3 with various compositions of PEO-ENR50 and vari-ous weight percentage of LiCF3SO3 were pre-pared by solution casting technique. The poly-mer electrolyte films were characterized using DSC, XRD and AC impedance spectroscopy. The SPE with the PEO-ENR50 composition of 70-30 shows the highest conductivity of 4.2 × 10-5 Scm-1 at the 15 wt.% of LiCF3SO3 compared with the other composition of PEO/ENR50. This composition was then chosen to investigate the effect of LiCF3SO3 on the thermal property, structure and conductivity of the electrolyte. The highest room temperature conductivity of 1.4 × 10-4 Scm-1 was achieved at 20 wt.% of LiCF3SO3. The conductivity result is supported by the DSC and XRD analysis which showed the semi- crystalline nature of PEO turning to amor-phous state due to the increase in LiCF3SO3 content.