The results of the investigation of the magnetic and structural properties of the alloy system Fe0.75–xSi0.25Sbx, where x = 0, 0.05, 0.1, 0.15, 0.2, and 0.25 synthesized by mechanical alloying followed by heat treatm...The results of the investigation of the magnetic and structural properties of the alloy system Fe0.75–xSi0.25Sbx, where x = 0, 0.05, 0.1, 0.15, 0.2, and 0.25 synthesized by mechanical alloying followed by heat treatment are described. The x-ray diffraction reveals that all samples crystallize in the DO3-type cubic phase structure. Substituting Fe by Sb led to a decrease in the lattice constant and the unit cell volume. The magnetic properties are investigated by vibrating sample magnetometer and show that all the samples are ferromagnetically ordered at room temperature. The Curie temperature is found to decrease linearly from (850 ± 5) K for the parent alloy to (620 ± 5) K for the alloyith x = 0.25. The saturation magnetizations at room temperature and at 100 K are found to decrease with increasing the antimony concentration. The above results indicate that Sb dissolves in the cubic structure of this alloy system.展开更多
A comprehensive study of the magnetic properties of Y3-2xCa2xFe5-xVxO12 (0 ≤ x ≤ 1) has been performed. The garnet ferrites samples were prepared by the ceramic technique, and X-ray diffraction analysis indicates th...A comprehensive study of the magnetic properties of Y3-2xCa2xFe5-xVxO12 (0 ≤ x ≤ 1) has been performed. The garnet ferrites samples were prepared by the ceramic technique, and X-ray diffraction analysis indicates the formation of single cubic phase. Vibrating sample magnetometry (VSM) and a superconducting quantum-interference device (SQUID) were used to measure the magnetic properties, especially the magnetization and thermo-magnetic behavior. The magnetization curves exhibit the typical characteristics of ferrimagnetic materials at both 4.2 K and at room temperature. The samples have a low coercivities (between 20 and 40 Oe) and saturation magnetizations as high as 36 emu/g at 4.2 K. The saturation magnetization decreases with V and Ca contents, reaching about 8 emu/g at 4.2 K (x = 1). For all samples, the saturation magnetization decreases with increasing temperature, whereas the Curie temperature increases for small values of x, from 557 K for x = 0 to a maximum of 590 K for x = 0.2. For larger values of x, it decreases and reaches 525 K for x = 1.0. The basic experimental trends reflect the occupancy of the tetrahedral 24d sites by vanadium in combination with the predominant intersublattice exchange constant Jad, although the nonzero magnetization at x = 1.0 indicates that about 10% of the substituted V atoms goes onto the octahedral 16a sites.展开更多
文摘The results of the investigation of the magnetic and structural properties of the alloy system Fe0.75–xSi0.25Sbx, where x = 0, 0.05, 0.1, 0.15, 0.2, and 0.25 synthesized by mechanical alloying followed by heat treatment are described. The x-ray diffraction reveals that all samples crystallize in the DO3-type cubic phase structure. Substituting Fe by Sb led to a decrease in the lattice constant and the unit cell volume. The magnetic properties are investigated by vibrating sample magnetometer and show that all the samples are ferromagnetically ordered at room temperature. The Curie temperature is found to decrease linearly from (850 ± 5) K for the parent alloy to (620 ± 5) K for the alloyith x = 0.25. The saturation magnetizations at room temperature and at 100 K are found to decrease with increasing the antimony concentration. The above results indicate that Sb dissolves in the cubic structure of this alloy system.
文摘A comprehensive study of the magnetic properties of Y3-2xCa2xFe5-xVxO12 (0 ≤ x ≤ 1) has been performed. The garnet ferrites samples were prepared by the ceramic technique, and X-ray diffraction analysis indicates the formation of single cubic phase. Vibrating sample magnetometry (VSM) and a superconducting quantum-interference device (SQUID) were used to measure the magnetic properties, especially the magnetization and thermo-magnetic behavior. The magnetization curves exhibit the typical characteristics of ferrimagnetic materials at both 4.2 K and at room temperature. The samples have a low coercivities (between 20 and 40 Oe) and saturation magnetizations as high as 36 emu/g at 4.2 K. The saturation magnetization decreases with V and Ca contents, reaching about 8 emu/g at 4.2 K (x = 1). For all samples, the saturation magnetization decreases with increasing temperature, whereas the Curie temperature increases for small values of x, from 557 K for x = 0 to a maximum of 590 K for x = 0.2. For larger values of x, it decreases and reaches 525 K for x = 1.0. The basic experimental trends reflect the occupancy of the tetrahedral 24d sites by vanadium in combination with the predominant intersublattice exchange constant Jad, although the nonzero magnetization at x = 1.0 indicates that about 10% of the substituted V atoms goes onto the octahedral 16a sites.