Effects of diffusion welding parameters on strength of welded joint based on particle reinforced alumini- um matrix composite Al2O3p/6061Al were studied by comparing with aluminium matrix alloy,Mecha- nism for ...Effects of diffusion welding parameters on strength of welded joint based on particle reinforced alumini- um matrix composite Al2O3p/6061Al were studied by comparing with aluminium matrix alloy,Mecha- nism for the loss of joint strength was analyzed.It was pointed out that the key processing parameters affecting the strength of joint was the welding temperature.The high quality joint can be successfully obtained with appropriate diffusion welding parameters.展开更多
Tensile strength of diffusion welded joint of aluminum matrix composite is very low due to its poor weld- ability.In this paper, solution and age treatments were conducted on the welded joint of Al2O3p/ 6061Al compo...Tensile strength of diffusion welded joint of aluminum matrix composite is very low due to its poor weld- ability.In this paper, solution and age treatments were conducted on the welded joint of Al2O3p/ 6061Al composite subjected to diffusion welding using Gleeble 1500 machine, and ensile strength and microstructure of welded joint aged at175℃ were measured and analyzed respectively, Results showed that aging precipitation of welded joint is promoted effectively because of redistribution of reinforcement and a few number of dislocations in the matrix of weld zone resulting from welding pressure,and hence tensile strength of welded joint is increased significantly after aging treatment.展开更多
文摘Effects of diffusion welding parameters on strength of welded joint based on particle reinforced alumini- um matrix composite Al2O3p/6061Al were studied by comparing with aluminium matrix alloy,Mecha- nism for the loss of joint strength was analyzed.It was pointed out that the key processing parameters affecting the strength of joint was the welding temperature.The high quality joint can be successfully obtained with appropriate diffusion welding parameters.
文摘Tensile strength of diffusion welded joint of aluminum matrix composite is very low due to its poor weld- ability.In this paper, solution and age treatments were conducted on the welded joint of Al2O3p/ 6061Al composite subjected to diffusion welding using Gleeble 1500 machine, and ensile strength and microstructure of welded joint aged at175℃ were measured and analyzed respectively, Results showed that aging precipitation of welded joint is promoted effectively because of redistribution of reinforcement and a few number of dislocations in the matrix of weld zone resulting from welding pressure,and hence tensile strength of welded joint is increased significantly after aging treatment.