A series of Mge10(AlþY)alloys with various weight ratios of Al to Y were cast to investigate the role of Al_(2)Y in grain refinement in MgeAleY ternary system.Thermal analysis combined with microstructural and ED...A series of Mge10(AlþY)alloys with various weight ratios of Al to Y were cast to investigate the role of Al_(2)Y in grain refinement in MgeAleY ternary system.Thermal analysis combined with microstructural and EDX analysis was used to determine the phase transformation temperatures during solidification process.Experimental results show that when the Al content is below 4 wt%,a peritectic reaction,LþAl_(2)Y/a-Mg,occurs after the intermetallic Al_(2)Y forms directly from the melt as a pro-peritectic phase.Once the Al content is above 4 wt%,an eutectic reaction occurs at a lower temperature.The presence of the pro-peritectic phase can lead to nucleation of a-Mg directly through a peritectic reaction although grain refining efficiency is also closely related to the active particle size.In the case where solidification does not involve a peritectic reaction,the growth restriction factor,quantitatively the Q-value,governs the grain refining efficiency.Higher Q-value corresponds to finer grains.展开更多
In the present study,the non-isothermal early stages of surface oxidation of liquid Mg-1%Y alloy during casting were studied under UPH argon,dry air,and air mixed with protective fluorine-bearing gases.The chemistry a...In the present study,the non-isothermal early stages of surface oxidation of liquid Mg-1%Y alloy during casting were studied under UPH argon,dry air,and air mixed with protective fluorine-bearing gases.The chemistry and morphology of the surface films were characterized by SEM and EDX analyses.The results indicate a layer of smooth and tightly coherent oxidation film composed of MgO and Y_(2)O_(3) formed on the molten Mg-Y alloy surface with 40-60 nm thickness under dry air.A dendritic/cellular microstructure is clearly visible with Y-rich second phases gathered in surface of the melt and precipitated along the grain/cell boundaries under all gas conditions.Under fluorine-bearing gas mixtures,the surface film was a mixed oxide and fluoride and more even;a flat and folded morphology can be seen under SF6 with oxide as dominated phase and under 1,1,1,2-tetra-fluoroethane,a smooth and compact surface film uniformly covering the inner surface of the bubble with equal oxide and fluoride thickness,which results in a film without any major defects.MgF_(2) phase appears to be the key characteristic of a good protective film.展开更多
基金The authors would like to thank the CSIRO Flagship in Light Metals and the CAST Cooperative Research Centre(CAST CRC)for financial support.
文摘A series of Mge10(AlþY)alloys with various weight ratios of Al to Y were cast to investigate the role of Al_(2)Y in grain refinement in MgeAleY ternary system.Thermal analysis combined with microstructural and EDX analysis was used to determine the phase transformation temperatures during solidification process.Experimental results show that when the Al content is below 4 wt%,a peritectic reaction,LþAl_(2)Y/a-Mg,occurs after the intermetallic Al_(2)Y forms directly from the melt as a pro-peritectic phase.Once the Al content is above 4 wt%,an eutectic reaction occurs at a lower temperature.The presence of the pro-peritectic phase can lead to nucleation of a-Mg directly through a peritectic reaction although grain refining efficiency is also closely related to the active particle size.In the case where solidification does not involve a peritectic reaction,the growth restriction factor,quantitatively the Q-value,governs the grain refining efficiency.Higher Q-value corresponds to finer grains.
文摘In the present study,the non-isothermal early stages of surface oxidation of liquid Mg-1%Y alloy during casting were studied under UPH argon,dry air,and air mixed with protective fluorine-bearing gases.The chemistry and morphology of the surface films were characterized by SEM and EDX analyses.The results indicate a layer of smooth and tightly coherent oxidation film composed of MgO and Y_(2)O_(3) formed on the molten Mg-Y alloy surface with 40-60 nm thickness under dry air.A dendritic/cellular microstructure is clearly visible with Y-rich second phases gathered in surface of the melt and precipitated along the grain/cell boundaries under all gas conditions.Under fluorine-bearing gas mixtures,the surface film was a mixed oxide and fluoride and more even;a flat and folded morphology can be seen under SF6 with oxide as dominated phase and under 1,1,1,2-tetra-fluoroethane,a smooth and compact surface film uniformly covering the inner surface of the bubble with equal oxide and fluoride thickness,which results in a film without any major defects.MgF_(2) phase appears to be the key characteristic of a good protective film.