A new numerical technique for testing and evaluation of quenching media and quenching systems is outlined. The measured time-temperature samples as a result of cooling curve test are analyzed by the new software devel...A new numerical technique for testing and evaluation of quenching media and quenching systems is outlined. The measured time-temperature samples as a result of cooling curve test are analyzed by the new software developed, in order to characterize quantitatively the quenchants. The method applied is based on Fourier analysis. Examples for evaluation and comparison of cooling performance of quenchants are presented the applicability of the computational technique.展开更多
The fatigue cracking behavior at twin boundaries(TBs)in a Co Cr Fe Mn Ni high-entropy alloy with three different grain sizes was systematically investigated under low-cycle fatigue.Irrespective of grain size,the chang...The fatigue cracking behavior at twin boundaries(TBs)in a Co Cr Fe Mn Ni high-entropy alloy with three different grain sizes was systematically investigated under low-cycle fatigue.Irrespective of grain size,the change from slip band cracking to TB cracking occurred with increasing the difference in the Schmid factors(DSF)between matrix and twin.However,the required critical DSF for the transition of the dominant cracking mode decreases with decreasing grain size due to the reduced slip band spacing that increases the impingement sites on the TBs and facilitates the coalescence of defects and voids to initiate TB cracks.展开更多
文摘A new numerical technique for testing and evaluation of quenching media and quenching systems is outlined. The measured time-temperature samples as a result of cooling curve test are analyzed by the new software developed, in order to characterize quantitatively the quenchants. The method applied is based on Fourier analysis. Examples for evaluation and comparison of cooling performance of quenchants are presented the applicability of the computational technique.
基金supported financially by the Australian Research Council(Nos.DE170100053 and DP190102243)the Open Foundation of State Key Laboratory of Powder Metallurgy at Central South University+1 种基金the National Natural Science Foundation of China(No.51771229)The University of Sydney under the Robinson Fellowship Scheme.
文摘The fatigue cracking behavior at twin boundaries(TBs)in a Co Cr Fe Mn Ni high-entropy alloy with three different grain sizes was systematically investigated under low-cycle fatigue.Irrespective of grain size,the change from slip band cracking to TB cracking occurred with increasing the difference in the Schmid factors(DSF)between matrix and twin.However,the required critical DSF for the transition of the dominant cracking mode decreases with decreasing grain size due to the reduced slip band spacing that increases the impingement sites on the TBs and facilitates the coalescence of defects and voids to initiate TB cracks.