Enhanced corrosion resistance of phytic acid coated magnesium by stearic acid treatment

A green chemical conversion coating for magnesium was obtained with a phytic acid solution. The microstructure and corrosion properties of phytic acid conversion coated magnesium were further improved by soaking in stearic acid solution. The phytic acid conversion coated magnesium after soaking in the stearic acid showed no micro-cracks and the surface became very smooth. The corrosion behavior of the uncoated and coated magnesium samples was studied by electrochemical methods. The corrosion resistance of the stearic acid treated sample was much higher than that of phytic acid conversion coated magnesium or uncoated magnesium. The electrochemical results indicated that the stearic acid treated coating provided effective corrosion protection to the magnesium sample.

功能梯度类金刚石薄膜的脉冲激光制备

长期以来 ,高质量的纯类金刚石薄膜的成功制备一直受其巨大内部压应力的阻碍 ,因为这种压应力导致严重的附着问题。厚度大于 50 0nm的类金刚石薄膜中的压应力常使薄膜与基体剥离。作者采用功能梯度的设计概念 ,应用准分子脉冲激光沉积方法 ,成功制备了厚度超过 1 0 μm的高质量类金刚石薄膜。薄膜中的SP3碳原子含量超过 6 0 %。纳米硬度测试表明 ,薄膜的弹性模量高达 50 0GPa ,纳米硬度高达 6 0GPa ,薄膜与基体间附着良好。证明功能梯度的设计概念可以用于制备较厚的超硬类金刚石薄膜。