To understand the solidification pathway and microstructure evolution of Mg-9Al-2Ca alloy,the cooling curve of the alloy solidified under furnace cooling was measured and the water-quenched samples were observed.The e...To understand the solidification pathway and microstructure evolution of Mg-9Al-2Ca alloy,the cooling curve of the alloy solidified under furnace cooling was measured and the water-quenched samples were observed.The experimental results show that the matrix phase of α-Mg dendrites is first generated at 596℃ during the solidification process,then the eutectic phases of Al_(2)Ca and Mg_(17)Al_(12) are formed at 518 and 447℃,respectively,and the solidification is terminated at 436℃.In the process of solidification,the seaweed dendrites of α-Mg get coarser and are gradually transformed into the global dendrites;besides,the secondary dendrite arms spacing(SDAS)of α-Mg as well as the solid fraction are both increased,while the increasing rate of SDAS of α-Mg and the solid fraction in the temperature region of 600-550℃ is faster than that in the temperature region of 550-436℃.And a power function relationship can be used to illustrate the change of the SDAS and the solid fraction with the temperature of solidification.展开更多
基金Funded by the Ph D Research Startup Foundation of Jining University(No.2017BSZX02)。
文摘To understand the solidification pathway and microstructure evolution of Mg-9Al-2Ca alloy,the cooling curve of the alloy solidified under furnace cooling was measured and the water-quenched samples were observed.The experimental results show that the matrix phase of α-Mg dendrites is first generated at 596℃ during the solidification process,then the eutectic phases of Al_(2)Ca and Mg_(17)Al_(12) are formed at 518 and 447℃,respectively,and the solidification is terminated at 436℃.In the process of solidification,the seaweed dendrites of α-Mg get coarser and are gradually transformed into the global dendrites;besides,the secondary dendrite arms spacing(SDAS)of α-Mg as well as the solid fraction are both increased,while the increasing rate of SDAS of α-Mg and the solid fraction in the temperature region of 600-550℃ is faster than that in the temperature region of 550-436℃.And a power function relationship can be used to illustrate the change of the SDAS and the solid fraction with the temperature of solidification.