Perovskite light-emitting diodes(PeLEDs)are considered as promising candidates for nextgeneration solution-processed full-color displays.However,the external quantum efficiencies(EQEs)and operational stabilities of de...Perovskite light-emitting diodes(PeLEDs)are considered as promising candidates for nextgeneration solution-processed full-color displays.However,the external quantum efficiencies(EQEs)and operational stabilities of deep-blue(<460 nm)PeLEDs still lag far behind their red and green counterparts.Herein,a rapid crystallization method based on hot-antisolvent bathing is proposed for realization of deep-blue PeLEDs.By promoting immediate removal of the precursor solvent from the wet perovskite films,development of the quasi-two-dimensional(2D)Ruddlesden–Popper perovskite(2D-RPP)crystals with n values>3 is hampered completely,so that phase-pure 2D-RPP films with bandgaps suitable for deep-blue PeLEDs can be obtained successfully.The uniquely developed rapid crystallization method also enables formation of randomly oriented 2D-RPP crystals,thereby improving the transfer and transport kinetics of the charge carriers.Thus,high-performance deep-blue PeLEDs emitting at 437 nm with a peak EQE of 0.63%are successfully demonstrated.The color coordinates are confirmed to be(0.165,0.044),which match well with the Rec.2020 standard blue gamut and have excellent spectral stability.展开更多
基金National R&D Program through the National Research Foundation of Korea(NRF)funded by the Ministry of Science and ICT(Grant Nos.2018M3D1A1058793 and 2021R1A3B1068920)the Yonsei Signature Research Cluster Program of 2021(Grant No.2021-22-0002).
文摘Perovskite light-emitting diodes(PeLEDs)are considered as promising candidates for nextgeneration solution-processed full-color displays.However,the external quantum efficiencies(EQEs)and operational stabilities of deep-blue(<460 nm)PeLEDs still lag far behind their red and green counterparts.Herein,a rapid crystallization method based on hot-antisolvent bathing is proposed for realization of deep-blue PeLEDs.By promoting immediate removal of the precursor solvent from the wet perovskite films,development of the quasi-two-dimensional(2D)Ruddlesden–Popper perovskite(2D-RPP)crystals with n values>3 is hampered completely,so that phase-pure 2D-RPP films with bandgaps suitable for deep-blue PeLEDs can be obtained successfully.The uniquely developed rapid crystallization method also enables formation of randomly oriented 2D-RPP crystals,thereby improving the transfer and transport kinetics of the charge carriers.Thus,high-performance deep-blue PeLEDs emitting at 437 nm with a peak EQE of 0.63%are successfully demonstrated.The color coordinates are confirmed to be(0.165,0.044),which match well with the Rec.2020 standard blue gamut and have excellent spectral stability.