Diffusion couples,WC/Co-1at.%C,V8C7/Co,and WC/Co-0.3wt.%V8C7 were constructed and annealed at temperatures ranging from 1100 to 1300℃. The concentration profile of V and W atoms in these couples were measured by EPMA...Diffusion couples,WC/Co-1at.%C,V8C7/Co,and WC/Co-0.3wt.%V8C7 were constructed and annealed at temperatures ranging from 1100 to 1300℃. The concentration profile of V and W atoms in these couples were measured by EPMA. Aided by Thermo-calc ＆ DICTRA software package,the concentration profiles of W and V in established diffusion couples were calculated by the moving boundary model according to revised dynamic parameters and MOB database,respectively. Then the concentration profile of W in Co binder during sintering WC-Co cemented carbide was simulated by the Cell model. It can provide reference for composition and sintering process design of cemented carbides with high performance. Meanwhile,the validity of revised dynamic parameters of the W-C-Co-V system is verified by the comparison of experimental and simulated results.展开更多
Thermodynamic assessment in the ternary systems ZrO2 -CeO2 -Y2 O3, ZrO2 -CeO2 -Ce2 03 and the limiting binaries ZrO2 -Y2 O3, ZrO2 -CeO2, CeO2 -Y2 03, ZrO2 -Ce2O3, CeO2 -Ce2O3 as well as the modeling for oxides are rev...Thermodynamic assessment in the ternary systems ZrO2 -CeO2 -Y2 O3, ZrO2 -CeO2 -Ce2 03 and the limiting binaries ZrO2 -Y2 O3, ZrO2 -CeO2, CeO2 -Y2 03, ZrO2 -Ce2O3, CeO2 -Ce2O3 as well as the modeling for oxides are reviewed comprehensively. Based on the recent estimations on the YO1.5-CeO2, ZrO2-CeO2 and ZrO2 -YO1.6 systems, isothermal sections at 1273 and 1 973 K of the ternary CeO2- ZrO2-YO1.5system are calculated. In the system of ZrO2-CeO2-Ce2O3, the complex relation between the nonstoichiometry （y） in CeO2-x, the composition of the ZrO2 -CeO2 solid solution and the oxygen partial pressure （Po2 ） for different ZrO2 containing solid solutions CexZr1-xO2-x. are evaluated from 1 473 to 1 773 K. The relation between the degree of Ce^＋4 reduction to Ce.3 under different Po2 in the fluorite CeO2-xy and CexZr1-xOz-x solid solutions at different temperatures can be used as a guide in the development of functional ceramics.展开更多
Three-dimensional atom probe （3DAP） technique has been used to study the nucleation and growth of M23C6 carbide in a supersaturated multi-component Fe-based alloy aged at 800℃. 3D images indicate that the radius of...Three-dimensional atom probe （3DAP） technique has been used to study the nucleation and growth of M23C6 carbide in a supersaturated multi-component Fe-based alloy aged at 800℃. 3D images indicate that the radius of M23C6 carbide after ageing for 10 min is about 9 nm. Concentration profiles of alloy elements in the carbide are also obtained. Combined with PANDAT and Thermo-Calc software, attempts to model the early stages of precipitation are present. The calculated particle size and composition of M23C6 carbide is in good agreement with 3DAP data.展开更多
基金the National Natural Science Foundation of China (No. 50471101)the Flan-ders-China Bilateral Project BIL 02/04.
文摘Diffusion couples,WC/Co-1at.%C,V8C7/Co,and WC/Co-0.3wt.%V8C7 were constructed and annealed at temperatures ranging from 1100 to 1300℃. The concentration profile of V and W atoms in these couples were measured by EPMA. Aided by Thermo-calc ＆ DICTRA software package,the concentration profiles of W and V in established diffusion couples were calculated by the moving boundary model according to revised dynamic parameters and MOB database,respectively. Then the concentration profile of W in Co binder during sintering WC-Co cemented carbide was simulated by the Cell model. It can provide reference for composition and sintering process design of cemented carbides with high performance. Meanwhile,the validity of revised dynamic parameters of the W-C-Co-V system is verified by the comparison of experimental and simulated results.
文摘Thermodynamic assessment in the ternary systems ZrO2 -CeO2 -Y2 O3, ZrO2 -CeO2 -Ce2 03 and the limiting binaries ZrO2 -Y2 O3, ZrO2 -CeO2, CeO2 -Y2 03, ZrO2 -Ce2O3, CeO2 -Ce2O3 as well as the modeling for oxides are reviewed comprehensively. Based on the recent estimations on the YO1.5-CeO2, ZrO2-CeO2 and ZrO2 -YO1.6 systems, isothermal sections at 1273 and 1 973 K of the ternary CeO2- ZrO2-YO1.5system are calculated. In the system of ZrO2-CeO2-Ce2O3, the complex relation between the nonstoichiometry （y） in CeO2-x, the composition of the ZrO2 -CeO2 solid solution and the oxygen partial pressure （Po2 ） for different ZrO2 containing solid solutions CexZr1-xO2-x. are evaluated from 1 473 to 1 773 K. The relation between the degree of Ce^＋4 reduction to Ce.3 under different Po2 in the fluorite CeO2-xy and CexZr1-xOz-x solid solutions at different temperatures can be used as a guide in the development of functional ceramics.
基金supported by the National Natural Science Foundation of China (Nos. 50971137 and 50934011)
文摘Three-dimensional atom probe （3DAP） technique has been used to study the nucleation and growth of M23C6 carbide in a supersaturated multi-component Fe-based alloy aged at 800℃. 3D images indicate that the radius of M23C6 carbide after ageing for 10 min is about 9 nm. Concentration profiles of alloy elements in the carbide are also obtained. Combined with PANDAT and Thermo-Calc software, attempts to model the early stages of precipitation are present. The calculated particle size and composition of M23C6 carbide is in good agreement with 3DAP data.