AIM:To investigate the distribution of intraocular pressure(IOP)and its relationship with refractive error and other factors in university students from Anyang,China.METHODS:A university-based study was conducted.Subjects were invited to complete ophthalmic examinations,including visual acuity,noncontact tonometr y(NCT),cycloplegic autorefraction,and ocular biometry.Univariable and multivariable analyses were used to evaluate the associations between IOP and other factors.Only data from right eyes were used in analysis.RESULTS:A total of 7720 subjects aged 16 to 26 years old were included,and 2834(36.4%)of the participants were male.The mean IOP of the right eye for all subjects was 15.52±3.20 mm Hg(95%CI:15.45,15.59).Using multivariate linear regression analysis,IOP was found to correlate significantly with younger age(P<0.001;standardized regression coefficientβ,-0.061;regression coefficientβ,-0.139;95%CI:-0.18,-0.09),higher myopic refractive error(P=0.044;standardizedβ,-0.060;regression coefficientβ,-0.770;95%CI:-0.15,-0.002),higher central corneal thickness(P<0.001;standardizedβ,0.450;regression coefficientβ,0.044;95%CI:0.04,0.05),and shorter axial length(AL;P<0.001;standardizedβ,-0.061;regression coefficientβ,-0.163;95%CI:-0.25,-0.07).CONCLUSION:This study described the normal distribution of IOP.In Chinese university students aged 16-26 y,higherIOP is associated with younger age,higher myopic refractive error,higher thickness of the central cornea,and shorter AL.

Synthesis of one-dimensional GaN nanorods by Tb intermediate layer with different thicknesses

GaN nanorods were synthesized by magnetron sputtering and ammonification system, and the thickness of Tb intermediate layer was changed to study the effect on GaN nanorods. The resultant was tested by scanning electron microscopy （SEM）, X-ray diffraction （XRD）, transmission electron microscopy （TEM）, high-resolution transmission electron microscopy （HRTEM）, and photo- luminescence （PL） spectra. The results show that the thickness of Tb layer has an evident effect on the modality, quality, and luminescence properties of GaN nanorods. PL spectra at room temperature show a very strong emission peak at 368 nm and a weak emission peak at 387 nm, and the intensities of the peak for the produced samples reach the maximum when Tb layer is 20 nm. Finally, the optimal thickness of 20 nm of Tb intermediate layer for synthe- sizing GaN nanostructures is achieved.