A novel single-phase Sm^3+activated Ca5(PO4)2SiO4 phosphor was successfully fabricated via a conventional solid-state method,which can be e fficie ntly excited by near ultraviolet(n-UV)light-emitting chips.The crystal...A novel single-phase Sm^3+activated Ca5(PO4)2SiO4 phosphor was successfully fabricated via a conventional solid-state method,which can be e fficie ntly excited by near ultraviolet(n-UV)light-emitting chips.The crystal structure and luminescence properties were characterized and analyzed systematically by using relevant instruments.The Ca5(PO4)2SiO4:Sm^3+phosphor shows an orange-red emission peaking at600 nm under the excitation of 403 nm and the optimal doping concentration of Sm^3+is determined to be 0.08,The critical distance of Ca5(PO4)2SiO4:0.08 Sm^3+is calculated to be 1.849 nm and concentration quenching mechanism of the Sm^3+in Ca5(PO4)2SiO4 host is ascribed to energy transfer between nearestneighbor activators.The decay time of Ca5(PO4)2 SiO4:0,08 Sm^3+is determined to be 1.1957 ms.In addition,the effect of temperature on the emission intensity was also studied,72.4%of the initial intensity is still preserved at 250℃,better thermal stability compared to commercial phosphor YAG:Ce^3+indicates that Ca5(PO4)2SiO4:0.08 Sm^3+has excellent thermal stability and active energy is deduced to be 0.130 eV.All the results demonstrate that orange-red emitting Ca5(PO4)2SiO4:0.08 Sm3+phosphor exhibits good luminescent properties.Owing to the excellent thermal quenching luminescence property,Ca5(PO4)2SiO4:0.08 Sm^3+phosphor can be applied in n-UV white light emitting diodes and serve as the warm part of white light.展开更多
基金supported by the Research Foundation for Youth Scholars of Beijing Technology and Business University (QNJJ2019-06,PXM2019_014213_000007)
文摘A novel single-phase Sm^3+activated Ca5(PO4)2SiO4 phosphor was successfully fabricated via a conventional solid-state method,which can be e fficie ntly excited by near ultraviolet(n-UV)light-emitting chips.The crystal structure and luminescence properties were characterized and analyzed systematically by using relevant instruments.The Ca5(PO4)2SiO4:Sm^3+phosphor shows an orange-red emission peaking at600 nm under the excitation of 403 nm and the optimal doping concentration of Sm^3+is determined to be 0.08,The critical distance of Ca5(PO4)2SiO4:0.08 Sm^3+is calculated to be 1.849 nm and concentration quenching mechanism of the Sm^3+in Ca5(PO4)2SiO4 host is ascribed to energy transfer between nearestneighbor activators.The decay time of Ca5(PO4)2 SiO4:0,08 Sm^3+is determined to be 1.1957 ms.In addition,the effect of temperature on the emission intensity was also studied,72.4%of the initial intensity is still preserved at 250℃,better thermal stability compared to commercial phosphor YAG:Ce^3+indicates that Ca5(PO4)2SiO4:0.08 Sm^3+has excellent thermal stability and active energy is deduced to be 0.130 eV.All the results demonstrate that orange-red emitting Ca5(PO4)2SiO4:0.08 Sm3+phosphor exhibits good luminescent properties.Owing to the excellent thermal quenching luminescence property,Ca5(PO4)2SiO4:0.08 Sm^3+phosphor can be applied in n-UV white light emitting diodes and serve as the warm part of white light.