In order to improve the comprehensive mechanical properties,deep cryogenic treatment(DCT)prior to aging was carried out on friction-stir-welded(FSW)2198 Al-Li alloy;afterward,the microstructure and tensile properties ...In order to improve the comprehensive mechanical properties,deep cryogenic treatment(DCT)prior to aging was carried out on friction-stir-welded(FSW)2198 Al-Li alloy;afterward,the microstructure and tensile properties were characterized by means of optical microscopy(OM),transmission electron microscopy(TEM)and tensile testing.The results show that FSW 2198 alloy through DCT prior to aging(DAT)possesses superior tensile properties than conventional aging treatment(AT)The microstructural analysis reveals that DAT alloy exhibits a finer grain structure,since DCT might effectively alleviate the residual stress in FSW 2198 alloy and thus decrease the driving force for grain coarsening in subsequent aging process.Moreover,DCT generates dislocation multiplication,which provides more preferential nucleation sites for T1(Al_(2)CuLi)phase during subsequent aging treatment,resulting in high-density fine T1 phases and thin precipitate-free zone within DAT alloy.Such reasonable microstructure leads to DAT alloy possessing better strength-ductility combination compared to AT alloy.展开更多
基金financially supported by the National Key Research and Development Program of China(No.2016YFB0300901)the National Natural Science Foundation of China(Nos.U1537212,51271011 and 51471019)。
文摘In order to improve the comprehensive mechanical properties,deep cryogenic treatment(DCT)prior to aging was carried out on friction-stir-welded(FSW)2198 Al-Li alloy;afterward,the microstructure and tensile properties were characterized by means of optical microscopy(OM),transmission electron microscopy(TEM)and tensile testing.The results show that FSW 2198 alloy through DCT prior to aging(DAT)possesses superior tensile properties than conventional aging treatment(AT)The microstructural analysis reveals that DAT alloy exhibits a finer grain structure,since DCT might effectively alleviate the residual stress in FSW 2198 alloy and thus decrease the driving force for grain coarsening in subsequent aging process.Moreover,DCT generates dislocation multiplication,which provides more preferential nucleation sites for T1(Al_(2)CuLi)phase during subsequent aging treatment,resulting in high-density fine T1 phases and thin precipitate-free zone within DAT alloy.Such reasonable microstructure leads to DAT alloy possessing better strength-ductility combination compared to AT alloy.