Three high-nitrogen stainless steels with different N contents were successfully processed by equal-channel angular pressing for one pass, and their microstructures and mechanical properties were investigated. It was ...Three high-nitrogen stainless steels with different N contents were successfully processed by equal-channel angular pressing for one pass, and their microstructures and mechanical properties were investigated. It was found that the microstructure of the billet was heterogeneous across the billet thickness, resulting in the difference in the mechanical properties due to the different deformation conditions. A relatively low strength, high uniform elongation, and high work- hardening rate for the samples at the bottom of the billet was achieved in comparison with those processed at the top. Meanwhile, it was observed that the density of deformation twins increased with the content of N; accordingly, the strength and elongation of the alloys increase with the content of N, resulting in a good strength-ductility combination.展开更多
The vermicular graphite iron is an important material with excellent combination properties for cylinder heads of diesel engines,and the high-temperature oxidation is a crucial problem during service of the component....The vermicular graphite iron is an important material with excellent combination properties for cylinder heads of diesel engines,and the high-temperature oxidation is a crucial problem during service of the component.In this study,the oxidation experiment of RuT400 vermicular graphite iron was performed at 500 ℃,and the oxidation time was chosen as 100 h,200 h,300 h,400 h,and 500 h,respectively.Meanwhile,the corresponding microstructure evolution,oxidation kinetics,and oxidation mechanism were discussed.It is found that oxidation pores and oxide layer often appear at the vermicular graphite on the specimen surface;the vermicular graphite plays the role of oxidation channel,and it tends to diff use along the adjacent pearlite and then connect with each other to form oxidation bridges as the oxidation time prolongs.A linear relationship between oxidation weight gain and the thickness of the oxide layer was established and verifi ed well.These results will give a more comprehensive understanding on the oxidation mechanism of vermicular graphite iron and provide certain guidance for design and preparation of anti-oxidation cast irons.展开更多
基金The National Natural Science Foundation of China(NSFC)under Grant Nos.5130117951331007+1 种基金31370976financially supported this work
文摘Three high-nitrogen stainless steels with different N contents were successfully processed by equal-channel angular pressing for one pass, and their microstructures and mechanical properties were investigated. It was found that the microstructure of the billet was heterogeneous across the billet thickness, resulting in the difference in the mechanical properties due to the different deformation conditions. A relatively low strength, high uniform elongation, and high work- hardening rate for the samples at the bottom of the billet was achieved in comparison with those processed at the top. Meanwhile, it was observed that the density of deformation twins increased with the content of N; accordingly, the strength and elongation of the alloys increase with the content of N, resulting in a good strength-ductility combination.
基金the National Natural Science Foundation of China (NSFC) under Grant.No.51871224the Natural Science Foundation of Liaoning Province under Grant.No.20180550880。
文摘The vermicular graphite iron is an important material with excellent combination properties for cylinder heads of diesel engines,and the high-temperature oxidation is a crucial problem during service of the component.In this study,the oxidation experiment of RuT400 vermicular graphite iron was performed at 500 ℃,and the oxidation time was chosen as 100 h,200 h,300 h,400 h,and 500 h,respectively.Meanwhile,the corresponding microstructure evolution,oxidation kinetics,and oxidation mechanism were discussed.It is found that oxidation pores and oxide layer often appear at the vermicular graphite on the specimen surface;the vermicular graphite plays the role of oxidation channel,and it tends to diff use along the adjacent pearlite and then connect with each other to form oxidation bridges as the oxidation time prolongs.A linear relationship between oxidation weight gain and the thickness of the oxide layer was established and verifi ed well.These results will give a more comprehensive understanding on the oxidation mechanism of vermicular graphite iron and provide certain guidance for design and preparation of anti-oxidation cast irons.