Through the method of initial heat release rate, the kinetic property of tyrosine oxidation catalyzed by tyrosinase from Pseudomonas maltophilia was investigated using a LKB-2107 batch microcalorimeter. Tyrosine was c...Through the method of initial heat release rate, the kinetic property of tyrosine oxidation catalyzed by tyrosinase from Pseudomonas maltophilia was investigated using a LKB-2107 batch microcalorimeter. Tyrosine was catalyzed and oxidized into L-dopa, then into melanin catalyzed by tyrosinase. We found that the tyrosinase reaction obeyed the Michaelis-Menten kinetics, and at 298.15K and pH 7.0, the initial exothermic rate (W0 ) are in the range of 0.1567~0.5704 mJ·s-1, the maximum exothermic rate (Wmax) are in 0.4152 ~ 0.8143mol·L-1, and mean value of the Michaelis constant (Km) is 2.199±0.105104 mol·L-1.展开更多
Sintering shrinkage, compressive strength, bending strength, chemical composition and their relationships with mi-crostructure of HA-Ti and HA-BG-Ti biomaterials were studied. The results show that sintering shrinkage...Sintering shrinkage, compressive strength, bending strength, chemical composition and their relationships with mi-crostructure of HA-Ti and HA-BG-Ti biomaterials were studied. The results show that sintering shrinkage curve of HA-BG-Ti composite changes just like S shape (23.1%-16.2%-21.8%-17.1%) with increase of Ti content, and sintering shrinkage of HA-BG-Ti composite is always higher than that of HA-Ti composite. The approach also indicates that compressive strength and bending strength of HA-BG-Ti composite are always higher than that of HA-Ti composite. Basically, with its compressive strength and bending strength equaling to 211.5 MPa and 132.1 MPa respectively, HA-10 vol. pct BG-60 vol. pct Ti composite can meet the mechanical properties requirements of the outer dense bulk. Furthermore, microstructure analysis shows that interfacial integration of HA-BG-Ti composite is better than that of HA-Ti composite. From X-ray diffraction (XRD) and SEM-EDAX analysis, brittle new phases including calcium titanate and calcium carbonate are detected in HA-Ti composite. New phases in HA-Ti composite and complex strong binding force accompanied by elemental diffusion of Si, Ti in HA-BG-Ti composite can explain theoretically the great difference of mechanical properties of HA-Ti and HA-BG-Ti composites.展开更多
基金This work were supported by the National Natural Science Foundation of China(No.30170010,29973030)The Teaching and Research Award Program for Outstanding Young Professors in High Education Institute,MOE,China(2001).
文摘Through the method of initial heat release rate, the kinetic property of tyrosine oxidation catalyzed by tyrosinase from Pseudomonas maltophilia was investigated using a LKB-2107 batch microcalorimeter. Tyrosine was catalyzed and oxidized into L-dopa, then into melanin catalyzed by tyrosinase. We found that the tyrosinase reaction obeyed the Michaelis-Menten kinetics, and at 298.15K and pH 7.0, the initial exothermic rate (W0 ) are in the range of 0.1567~0.5704 mJ·s-1, the maximum exothermic rate (Wmax) are in 0.4152 ~ 0.8143mol·L-1, and mean value of the Michaelis constant (Km) is 2.199±0.105104 mol·L-1.
基金The authors are grateful for the financial support from the National Natural Science Foundation of China(No.50174059).
文摘Sintering shrinkage, compressive strength, bending strength, chemical composition and their relationships with mi-crostructure of HA-Ti and HA-BG-Ti biomaterials were studied. The results show that sintering shrinkage curve of HA-BG-Ti composite changes just like S shape (23.1%-16.2%-21.8%-17.1%) with increase of Ti content, and sintering shrinkage of HA-BG-Ti composite is always higher than that of HA-Ti composite. The approach also indicates that compressive strength and bending strength of HA-BG-Ti composite are always higher than that of HA-Ti composite. Basically, with its compressive strength and bending strength equaling to 211.5 MPa and 132.1 MPa respectively, HA-10 vol. pct BG-60 vol. pct Ti composite can meet the mechanical properties requirements of the outer dense bulk. Furthermore, microstructure analysis shows that interfacial integration of HA-BG-Ti composite is better than that of HA-Ti composite. From X-ray diffraction (XRD) and SEM-EDAX analysis, brittle new phases including calcium titanate and calcium carbonate are detected in HA-Ti composite. New phases in HA-Ti composite and complex strong binding force accompanied by elemental diffusion of Si, Ti in HA-BG-Ti composite can explain theoretically the great difference of mechanical properties of HA-Ti and HA-BG-Ti composites.