In this paper,ordered mesoporous alumina(OMA)support with the high surface area(328 m^(2)g^(-1))and the large pore volume 0.74(cm^(3)·g^(-1))was synthesized by homogeneous precipitation method.And the influence o...In this paper,ordered mesoporous alumina(OMA)support with the high surface area(328 m^(2)g^(-1))and the large pore volume 0.74(cm^(3)·g^(-1))was synthesized by homogeneous precipitation method.And the influence of EDTA on the physical and chemical properties of the modified catalysts was also studied.The characteristic results showed that the addition of EDTA could adjust the metal-support interaction and improved the acidity of the corresponding catalyst.Combined with the catalytic performance results,the EDTA-modified Ni Mo E(1.0)/OMA catalyst displays the highest DBT hydrodesulfurization conversion(97.7%).展开更多
Hierarchically porous Beta/SBA-16(BS)composite materials,combining the characteristics of the acidity from the Beta zeolite and the three-dimensional structure from SBA-16,were synthesized successfully through a two-s...Hierarchically porous Beta/SBA-16(BS)composite materials,combining the characteristics of the acidity from the Beta zeolite and the three-dimensional structure from SBA-16,were synthesized successfully through a two-step in-situ assembly hydrothermal crystallization method.A series of Ni Mo catalysts supported on BS with different silica-alumina ratios were prepared.The supports and the corresponding catalysts were characterized by XRD,N_(2) physisorption,^(27)Al MAS NMR,TEM,pyridine-FTIR,Raman,XPS and HRTEM.The activities of series catalysts were evaluated by the hydrodesulfurization(HDS)performances of dibenzothiophene(DBT)and 4,6-dimethyldibenzothiophene(4,6-DMDBT).It was found that the Beta crystallites were embedded into SBA-16 through silanols accompanied by dealumination on the T3-T9 sites of Beta crystallites.Ni Mo/BS-3 with a silica-alumina ratio of 100 exhibited the highest DBT and 4,6-DMDBT HDS activities at the WHSV value of 10 h^(-1),with the conversions of 95.9%and 86.9%respectively,due to the synergistic effects of the suitable specific surface areas,the relatively large pore size,appropriate acidity,the relatively high sulfidation degree,moderate dispersity and good stacking degree of Mo S;active phases.展开更多
基金financially supported by the National Natural Science Foundation of China(No.21878330,21676298)the National Key R&D Program of China(2019YFC1907602)the CNPC Key Research Project(2016E-0707)。
文摘In this paper,ordered mesoporous alumina(OMA)support with the high surface area(328 m^(2)g^(-1))and the large pore volume 0.74(cm^(3)·g^(-1))was synthesized by homogeneous precipitation method.And the influence of EDTA on the physical and chemical properties of the modified catalysts was also studied.The characteristic results showed that the addition of EDTA could adjust the metal-support interaction and improved the acidity of the corresponding catalyst.Combined with the catalytic performance results,the EDTA-modified Ni Mo E(1.0)/OMA catalyst displays the highest DBT hydrodesulfurization conversion(97.7%).
基金supported by the National Natural Science Foundation of China(No.21878330,21676298)the National Science and Technology Major Project(No.2019YFC1907700)+1 种基金the CNPC Key Research Project(2016E-0707)the King Abdullah University of Science and Technology(KAUST)。
文摘Hierarchically porous Beta/SBA-16(BS)composite materials,combining the characteristics of the acidity from the Beta zeolite and the three-dimensional structure from SBA-16,were synthesized successfully through a two-step in-situ assembly hydrothermal crystallization method.A series of Ni Mo catalysts supported on BS with different silica-alumina ratios were prepared.The supports and the corresponding catalysts were characterized by XRD,N_(2) physisorption,^(27)Al MAS NMR,TEM,pyridine-FTIR,Raman,XPS and HRTEM.The activities of series catalysts were evaluated by the hydrodesulfurization(HDS)performances of dibenzothiophene(DBT)and 4,6-dimethyldibenzothiophene(4,6-DMDBT).It was found that the Beta crystallites were embedded into SBA-16 through silanols accompanied by dealumination on the T3-T9 sites of Beta crystallites.Ni Mo/BS-3 with a silica-alumina ratio of 100 exhibited the highest DBT and 4,6-DMDBT HDS activities at the WHSV value of 10 h^(-1),with the conversions of 95.9%and 86.9%respectively,due to the synergistic effects of the suitable specific surface areas,the relatively large pore size,appropriate acidity,the relatively high sulfidation degree,moderate dispersity and good stacking degree of Mo S;active phases.