In order to improve the mechanical properties of Mg-Li alloy with single β phase structure, Mg-12Li-3Al-xNd(x=0.3, 0.7, 1.1, 2.0wt.%) alloy was prepared. Subsequently, the as-cast microstructure and mechanical proper...In order to improve the mechanical properties of Mg-Li alloy with single β phase structure, Mg-12Li-3Al-xNd(x=0.3, 0.7, 1.1, 2.0wt.%) alloy was prepared. Subsequently, the as-cast microstructure and mechanical properties were observed and tested. The results showed that the structure of Mg-12Li-3Al-xNd(x=0.3, 0.7, 1.1, 2.0wt.%) as-cast alloy was composed of β phase matrix and Al_2Nd, Al_(11)Nd_3, MgLiAl_2, Al_4Li_9 and AlLi phases. With the increase of Nd content in the alloy, the Al-Nd intermetallic compounds have a trend to change from needle-like Al_(11)Nd_3 to granular Al_2Nd. The hardness of as-cast Mg-12Li-3Al-xNd(x=0.3, 0.7, 1.1, 2.0wt.%) alloy was stable at room temperature. The tensile strength of Mg-12Li-3Al-1.1Nd was as high as 180 MPa, the elongation rate of Mg-12Li-3Al-0.7Nd reached 53.7%, and the comprehensive mechanical properties of Mg-12Li-3Al-2.0Nd was the best. PLC phenomenon occurred during the tensile process of the alloys at room temperature. Therefore, the β-based Mg-Li alloy with good plasticity as well as enhanced strength can be obtained by a moderate addition of Nd and Al.展开更多
基金financially supported by the Science and Technology Research Project for Colleges and Universities of Hebei Province(ZD2014040)
文摘In order to improve the mechanical properties of Mg-Li alloy with single β phase structure, Mg-12Li-3Al-xNd(x=0.3, 0.7, 1.1, 2.0wt.%) alloy was prepared. Subsequently, the as-cast microstructure and mechanical properties were observed and tested. The results showed that the structure of Mg-12Li-3Al-xNd(x=0.3, 0.7, 1.1, 2.0wt.%) as-cast alloy was composed of β phase matrix and Al_2Nd, Al_(11)Nd_3, MgLiAl_2, Al_4Li_9 and AlLi phases. With the increase of Nd content in the alloy, the Al-Nd intermetallic compounds have a trend to change from needle-like Al_(11)Nd_3 to granular Al_2Nd. The hardness of as-cast Mg-12Li-3Al-xNd(x=0.3, 0.7, 1.1, 2.0wt.%) alloy was stable at room temperature. The tensile strength of Mg-12Li-3Al-1.1Nd was as high as 180 MPa, the elongation rate of Mg-12Li-3Al-0.7Nd reached 53.7%, and the comprehensive mechanical properties of Mg-12Li-3Al-2.0Nd was the best. PLC phenomenon occurred during the tensile process of the alloys at room temperature. Therefore, the β-based Mg-Li alloy with good plasticity as well as enhanced strength can be obtained by a moderate addition of Nd and Al.