Significant electric control of exchange bias effect in a simple CoO1-δ/Co system, grown on piezoelectric Pb(Mg1/3Nb2/3)0.7Ti0.3O3 (110) (PMN-PT) substrates, is achieved at room temperature. Obvious changes in both t...Significant electric control of exchange bias effect in a simple CoO1-δ/Co system, grown on piezoelectric Pb(Mg1/3Nb2/3)0.7Ti0.3O3 (110) (PMN-PT) substrates, is achieved at room temperature. Obvious changes in both the coercivity field (HC) and the exchange bias field (HE), of 31% and 5%, respectively, have been observed when the electric field is applied to the substrate. While the change of coercivity is related to the enhanced uniaxial anisotropy in the ferromagnetic layer, the change of the exchange bias field can only originate from the spin reorientation in the antiferromagnetic CoO1-δ layer caused by the strain-induced magnetoelastic effect. A large HE/HC > 2, and HE~ 110 Oe at room temperature, as well as the low-energy fabrication of this system, make it a practical system for spintronic device applications.展开更多
To investigate the process of strain relaxation and resultant variation of microstructure and magnetic properties,low-doped La_(0.825)Sr_(0.175)MnO_3 epitaxial films with different thicknesses are deposited on LaAlO_3...To investigate the process of strain relaxation and resultant variation of microstructure and magnetic properties,low-doped La_(0.825)Sr_(0.175)MnO_3 epitaxial films with different thicknesses are deposited on LaAlO_3 substrates and strain induced nanopillars are discovered inside the La_(0.825) Sr_(0.175)MnO_3 film. Perpendicular oriented nanopillars mainly exist below 30 nm and tend to disappear above 30 nm. The distribution of nanopillars not only induce the variation of lattice parameters and local structural distortion but also lead to the deviation of easy magnetization axis from the perpendicular direction. Specifically, the out-of-plane lattice parameters of the film decrease quickly with the increase of the thickness but tend to be constant when the thickness is above 30 nm. Meanwhile, the variations of magnetic properties along in-plane and out-of-plane directions would also decline at first and they then remain nearly unchanged. Our work constructs the relationship between nanopillars and magnetic properties inside films. We are able to clearly reveal the effects of inhomogeneous strain relaxation.展开更多
基金Project supported by the National Key R&D Program of China(Grant Nos.2017YFA0206303 and 2017YFA020630)the National Natural Science Foundation of China(Grant Nos.11975035 and 51731001).
文摘Significant electric control of exchange bias effect in a simple CoO1-δ/Co system, grown on piezoelectric Pb(Mg1/3Nb2/3)0.7Ti0.3O3 (110) (PMN-PT) substrates, is achieved at room temperature. Obvious changes in both the coercivity field (HC) and the exchange bias field (HE), of 31% and 5%, respectively, have been observed when the electric field is applied to the substrate. While the change of coercivity is related to the enhanced uniaxial anisotropy in the ferromagnetic layer, the change of the exchange bias field can only originate from the spin reorientation in the antiferromagnetic CoO1-δ layer caused by the strain-induced magnetoelastic effect. A large HE/HC > 2, and HE~ 110 Oe at room temperature, as well as the low-energy fabrication of this system, make it a practical system for spintronic device applications.
基金the National Key Research and Development Program of China under Grant Nos 2017YFA206303 and 2016YFB0700901the National Natural Science Foundation of China under Grant Nos 51731001,51371009 and 51271004
文摘To investigate the process of strain relaxation and resultant variation of microstructure and magnetic properties,low-doped La_(0.825)Sr_(0.175)MnO_3 epitaxial films with different thicknesses are deposited on LaAlO_3 substrates and strain induced nanopillars are discovered inside the La_(0.825) Sr_(0.175)MnO_3 film. Perpendicular oriented nanopillars mainly exist below 30 nm and tend to disappear above 30 nm. The distribution of nanopillars not only induce the variation of lattice parameters and local structural distortion but also lead to the deviation of easy magnetization axis from the perpendicular direction. Specifically, the out-of-plane lattice parameters of the film decrease quickly with the increase of the thickness but tend to be constant when the thickness is above 30 nm. Meanwhile, the variations of magnetic properties along in-plane and out-of-plane directions would also decline at first and they then remain nearly unchanged. Our work constructs the relationship between nanopillars and magnetic properties inside films. We are able to clearly reveal the effects of inhomogeneous strain relaxation.