Microstructure and mechanical properties of twin-wire arc sprayed Ni-Al composite coatings on 6061-T6 aluminum alloy sheet

We have systematically studied the microstructure and mechanical properties of Ni-5wt%Al and Ni-20wt%Al composite coat- ings fabricated on 6061-T6 aluminum alloy sheet by twin-wire arc spraying under different experimental conditions. The abrasive wear be- havior and interface diffusion behavior of the composite coatings were evaluated by dry/wet rubber wheel abrasive wear tests and heat treat- ment, respectively. Experimental results indicate that the composite coatings exhibit features of adhesive wear. Besides, the Vickers micro- hardness of NiA1 and Ni3AI intermetallic compounds is relatively larger than that of the substrate, which is beneficial for enhancing the wear resistance. With the increase of annealing temperature and time, the interface diffusion area between the Ni-Al coating and the substrate gradually expands with the formation of NiAl3 and Ni2Al3 phases, and is controlled by diffusion of aluminum atoms. The grain growth ex- ponent n of diffusion kinetics of the Ni-Al coating, calculated via a high-temperature diffusion model at 400, 480, and 550℃, is between 0.28 and 0.38. This satisfies the cubic law, which is consistent with the general theoretical relationship of high-temperature diffusion.

Microstructure of Ni–Al powder and Ni–Al composite coatings prepared by twin-wire arc spraying

Ni–Al powder and Ni–Al composite coatings were fabricated by twin-wire arc spraying（TWAS）. The microstructures of Ni-5wt%Al powder and Ni-20wt%Al powder were characterized by scanning electronic microscopy（SEM） and energy dispersive spectroscopy（EDS）. The results showed that the obtained particle size ranged from 5 to 50 μm. The morphology of the Ni–Al powder showed that molten particles were composed of Ni solid solution, NiAl, Ni_3Al, Al_2O_3, and NiO. The Ni–Al phase and a small amount of Al_2O_3 particles changed the composition of the coating. The microstructures of the twin-wire-arc-sprayed Ni–Al composite coatings were characterized by SEM, EDS, X-ray diffraction（XRD）, and transmission electron microscopy（TEM）. The results showed that the main phase of the Ni-5wt%Al coating consisted of Ni solid solution and Ni Al in addition to a small amount of Al_2O_3. The main phase of the Ni-20wt%Al coating mainly consisted of Ni solid solution, Ni Al, and Ni_3Al in addition to a small amount of Al and Al_2O_3, and Ni Al and Ni_3Al intermetallic compounds effectively further improved the final wear property of the coatings. TEM analysis indicated that fine spherical NiAl_3 precipitates and a Ni–Al–O amorphous phase formed in the matrix of the Ni solid solution in the original state.

Tensile properties and fracture reliability of a glass-coated Co-based amorphous microwire

Co68.15Fe4.35Si12.25B15.25 （at%） amorphous microwires with a smooth surface and a circular cross-section were fabricated by the glass-coated melt spinning method. Their mechanical properties were evaluated through tensile tests of the glass-coated amorphous mi-crowires, and their fracture reliability was estimated using two-and three-parameter Weibull analysis. X-ray diffraction and transmission electron microscopy results showed that these glass-coated Co-based microwires were mostly amorphous. The coated Co-based microwires exhibit a tensile strength of 1145 to 2457 MPa, with a mean value of 1727 MPa and a variance of 445 MPa. Weibull statistical analysis showed that the tensile two-parameter Weibull modulus of the amorphous microwires is 4.16 and the three-parameter Weibull modulus is 1.61 with a threshold value as high as 942 MPa. These results indicate that the fabricated microwires exhibit good tensile properties and fracture reliability, and thus appear to be good candidates for electronics reliability engineering applications.

Microstructure Evolution and Mechanical Properties of Spray-deposited Al-21.47Si-4.73Fe-2.5Cu-0.9Mg Alloy

Al-Si-Fe-Cu-Mg alloy was prepared by spray deposition and was further processed by hot extrusion as well as T6heat-treatment.The results indicate that the microstructure of the deposited alloy is composed of primary Si particles with average size of less than 5μm,α-Al,Al_2CuMg,β-Al_5FeSi andδ-Al_4FeSi_2（rectangular shape）,and no eutectic silicon is found due to the special solidification behavior.The age hardening curves reveal two peaks.The uniform ultimate tensile strength（UTS）and the elongation of the peak-aged Al-Si-Fe-Cu-Mg alloy are 468.3 MPa,0.61% at 298 Kand 267.4MPa,6.42% at 573 K,respectively.The fracture surfaces display brittle fracture morphology at 298 K,whereas it varies to mixture of brittle and ductile failure with increasing the temperature.

Effect of Double Oxide Film Defects on Mechanical Properties of As-Cast C95800 Alloy

The morphology of double oxide film defects and their influence on the tensile mechanical properties of a commercial Cu-Al （C95800） alloy were investigated in this study. Plane castings were produced with two types of pouting systems, and their tensile properties were measured and then analyzed by means of Weibull statistics method. The fracture surfaces of the tensile specimens were examined using scanning electron microscopy equipped with energy-dispersive spectroscopy. A large amount of double oxide film defects were observed on the tensile fractured specimens of the topfilled plane castings, and their chemical composition is identified to be Al2O3. Weibull statistics analyses showed that the double oxide film defects significantly reduce mechanical properties of the castings investigated. Furthermore, the ultimate tensile strength is more obviously deteriorated by double oxide film defects than elongation.