A water-quenching technique has been adopted to evaluate thermal shock fracture and fatigue behaviors of porous Si3N4 ceramics in an air atmosphere. The high-porosity Si3N4 ceramics exhibit a higher strength retention...A water-quenching technique has been adopted to evaluate thermal shock fracture and fatigue behaviors of porous Si3N4 ceramics in an air atmosphere. The high-porosity Si3N4 ceramics exhibit a higher strength retention and a better resistance to thermal shock fatigue because of its role of the pores as crack arresters.A dense and coherent surface oxide layer leads to a significant benefit in residual strength during thermal fatigue, however, an increased fatigue number to 30 th cycle cannot cause a further influence although a thicker oxide layer presents, which is attributed to holes defect and disappearance of part intergranular phase.展开更多
基金financial support of the project from the National Natural Science Foundation of China (Nos. 51272206 and 51472198)the Program for Changjiang Scholars and Innovative Research Team in University (No. IRT1280)+2 种基金the National Key Laboratory Functional Composite (No. 9140C560109130C56201)the Fundamental Research Funds for the Central University (No. xkjc2014009)the State Key Laboratory for Mechanical Behavior of Materials (No. 20121207)
文摘A water-quenching technique has been adopted to evaluate thermal shock fracture and fatigue behaviors of porous Si3N4 ceramics in an air atmosphere. The high-porosity Si3N4 ceramics exhibit a higher strength retention and a better resistance to thermal shock fatigue because of its role of the pores as crack arresters.A dense and coherent surface oxide layer leads to a significant benefit in residual strength during thermal fatigue, however, an increased fatigue number to 30 th cycle cannot cause a further influence although a thicker oxide layer presents, which is attributed to holes defect and disappearance of part intergranular phase.