The relation between the structure of the silver network electrodes and the properties of Cu(In,Ga)Se_(2)(CIGS)solar cells is systemically investigated.The Ag network electrode is deposited onto an Al:ZnO(AZO)thin fil...The relation between the structure of the silver network electrodes and the properties of Cu(In,Ga)Se_(2)(CIGS)solar cells is systemically investigated.The Ag network electrode is deposited onto an Al:ZnO(AZO)thin film,employing a self-forming cracked template.Precise control over the cracked template's structure is achieved through careful adjustment of temperature and humidity.The Ag network electrodes with different coverage areas and network densities are systemically applied to the CIGS solar cells.It is revealed that predominant fill factor(FF)is influenced by the figure of merit of transparent conducting electrodes,rather than sheet resistance,particularly when the coverage area falls within the range of 1.3–5%.Furthermore,a higher network density corresponds to an enhanced FF when the coverage areas of the Ag networks are similar.When utilizing a thinner AZO film,CIGS solar cells with a surface area of 1.0609 cm^(2)exhibit a notable performance improvement,with efficiency increasing from 10.48%to 11.63%.This enhancement is primarily attributed to the increase in FF from 45%to 65%.These findings underscore the considerable potential for reducing the thickness of the transparent conductive oxide(TCO)in CIGS modules with implications for practical applications in photovoltaic technology.展开更多
基金the National Research Foundation of Korea(NRF)The specific grants that facilitated this study include No.2021R1A5A8033165,RS-2023-00249229,2022M3J1A1085371,and 2023R1A2C1007386+1 种基金supported by the Human Resource Program in Energy Technology of the Korea Institute of Energy Technology Evaluation and Planning(KETEP),under grant No.20214000000200funded by the Ministry of Science and ICT(MSIT),the Ministry of Education,and the Ministry of Trade,Industry&Energy of the Republic of Korea.
文摘The relation between the structure of the silver network electrodes and the properties of Cu(In,Ga)Se_(2)(CIGS)solar cells is systemically investigated.The Ag network electrode is deposited onto an Al:ZnO(AZO)thin film,employing a self-forming cracked template.Precise control over the cracked template's structure is achieved through careful adjustment of temperature and humidity.The Ag network electrodes with different coverage areas and network densities are systemically applied to the CIGS solar cells.It is revealed that predominant fill factor(FF)is influenced by the figure of merit of transparent conducting electrodes,rather than sheet resistance,particularly when the coverage area falls within the range of 1.3–5%.Furthermore,a higher network density corresponds to an enhanced FF when the coverage areas of the Ag networks are similar.When utilizing a thinner AZO film,CIGS solar cells with a surface area of 1.0609 cm^(2)exhibit a notable performance improvement,with efficiency increasing from 10.48%to 11.63%.This enhancement is primarily attributed to the increase in FF from 45%to 65%.These findings underscore the considerable potential for reducing the thickness of the transparent conductive oxide(TCO)in CIGS modules with implications for practical applications in photovoltaic technology.
