Hydrogenated amorphous silicon oxide(a-SiOx:H) is an attractive passivation material to suppress epitaxial growth and reduce the parasitic absorption loss in silicon heterojunction(SHJ) solar cells. In this paper, a-S...Hydrogenated amorphous silicon oxide(a-SiOx:H) is an attractive passivation material to suppress epitaxial growth and reduce the parasitic absorption loss in silicon heterojunction(SHJ) solar cells. In this paper, a-SiOx:H layers on different orientated c-Si substrates are fabricated. An optimal effective lifetime(τ(eff)) of 4743 μs and corresponding implied opencircuit voltage(iV(oc)) of 724 mV are obtained on〈100〉-orientated c-Si wafers. While τ(eff) of 2429 μs and iV_(oc) of 699 mV are achieved on 111-orientated substrate. The FTIR and XPS results indicate that the a-SiOx:H network consists of SiOx(Si-rich), Si–OH, Si–O–SiHx, SiO2 ≡ Si–Si, and O3 ≡ Si–Si. A passivation evolution mechanism is proposed to explain the different passivation results on different c-Si wafers. By modulating the a-SiOx:H layer, the planar silicon heterojunction solar cell can achieve an efficiency of 18.15%.展开更多
基金Project supported by the National Key Research and Deveopment Program of China(Grant No.2018YFB1500402)the National Natural Science Foundation of China(Grant Nos.61674084 and 61874167)+5 种基金the Fundamental Research Funds for Central Universities,Chinathe Natural Science Foundation of Tianjin City,China(Grant No.17JCYBJC41400)the Open Fund of the Key Laboratory of Optical Information Science&Technology of Ministry of Education of China(Grant No.2017KFKT014)the 111 Project,China(Grant No.B16027)the International Cooperation Base,China(Grant No.2016D01025)Tianjin International Joint Research and Development Center,China。
文摘Hydrogenated amorphous silicon oxide(a-SiOx:H) is an attractive passivation material to suppress epitaxial growth and reduce the parasitic absorption loss in silicon heterojunction(SHJ) solar cells. In this paper, a-SiOx:H layers on different orientated c-Si substrates are fabricated. An optimal effective lifetime(τ(eff)) of 4743 μs and corresponding implied opencircuit voltage(iV(oc)) of 724 mV are obtained on〈100〉-orientated c-Si wafers. While τ(eff) of 2429 μs and iV_(oc) of 699 mV are achieved on 111-orientated substrate. The FTIR and XPS results indicate that the a-SiOx:H network consists of SiOx(Si-rich), Si–OH, Si–O–SiHx, SiO2 ≡ Si–Si, and O3 ≡ Si–Si. A passivation evolution mechanism is proposed to explain the different passivation results on different c-Si wafers. By modulating the a-SiOx:H layer, the planar silicon heterojunction solar cell can achieve an efficiency of 18.15%.