Mg−9Al−1Zn(AZ91)magnesium matrix composites reinforced by Ti−6Al−4V(TC4)particles were successfully prepared via powder metallurgical method.The yield strength(YS),ultimate tensile strength(UTS),and elongation(EL)show...Mg−9Al−1Zn(AZ91)magnesium matrix composites reinforced by Ti−6Al−4V(TC4)particles were successfully prepared via powder metallurgical method.The yield strength(YS),ultimate tensile strength(UTS),and elongation(EL)showed a mountain-like tendency with the increase of the TC4 content.The mechanical properties of AZ91 magnesium matrix composites reached the optimal point with TC4 content of 10 wt.%,realizing YS,UTS,and EL of 335 MPa,370 MPa,and 6.4%,respectively.The improvement of mechanical properties can be attributed to the effective load transfer from the magnesium matrix to the TC4 particles,dislocations associated with the difference in the coefficient of thermal expansion,good interfacial bonding between the Mg matrix and TC4 particles,and grain refinement strengthening.展开更多
In this study,the deformable titanium(Ti)particles reinforced AZ91 composite was successfully prepared by powder metallurgy and subsequent extrusion.The mechanical properties and microstructural evolution of pure AZ91...In this study,the deformable titanium(Ti)particles reinforced AZ91 composite was successfully prepared by powder metallurgy and subsequent extrusion.The mechanical properties and microstructural evolution of pure AZ91 and 5 Ti/AZ91 composite were studied.The yield strength,ultimate tensile strength,and elongation of 5 Ti/AZ91 composite are measured to be 212 MPa,323 MPa,and 10.1%,respectively.Microstructure analysis revealed that Ti particles are elongated along the extrusion direction,forming a discontinuous strip Ti particles,fine precipitated Mg_(17)Al_(12) phase inhibits dynamic recrystallization(DRX)behavior through Zener pinning effect and hinders the growth of matrix grains,resulting in refiner grains of 5 Ti/AZ91 composite.Heterogeneous deformed Ti particles and magnesium(Mg)matrix to generate additional heterogeneous deformation-induced(HDI)strengthening.Heterogeneous deformation-induced strengthening mainly contributed to the increment of yield strength for 5 Ti/AZ91 composite.展开更多
基金Acknowledgments The authors acknowledge the financial support from the Guangdong Major Project of Basic and Applied Basic Research,China(No.2020B0301030006)the National Natural Science Foundation of China(Nos.52171133,52171103)+1 种基金the“111 Project”by the Ministry of Education of China(No.B16007)Fundamental Research Fund of Central Universities in China(No.2018CDJDCL0019)。
文摘Mg−9Al−1Zn(AZ91)magnesium matrix composites reinforced by Ti−6Al−4V(TC4)particles were successfully prepared via powder metallurgical method.The yield strength(YS),ultimate tensile strength(UTS),and elongation(EL)showed a mountain-like tendency with the increase of the TC4 content.The mechanical properties of AZ91 magnesium matrix composites reached the optimal point with TC4 content of 10 wt.%,realizing YS,UTS,and EL of 335 MPa,370 MPa,and 6.4%,respectively.The improvement of mechanical properties can be attributed to the effective load transfer from the magnesium matrix to the TC4 particles,dislocations associated with the difference in the coefficient of thermal expansion,good interfacial bonding between the Mg matrix and TC4 particles,and grain refinement strengthening.
基金financially supported by the Guangdong Major Project of Basic and Applied Basic Research(No.2020B0301030006)the National Natural Science Foundation of China(Nos.52171133 and 52171103)the“111 Project”(B16007)by the Ministry of Education and Fundamental Research Fund of Central Universities in China(No.2018CDJDCL0019)。
文摘In this study,the deformable titanium(Ti)particles reinforced AZ91 composite was successfully prepared by powder metallurgy and subsequent extrusion.The mechanical properties and microstructural evolution of pure AZ91 and 5 Ti/AZ91 composite were studied.The yield strength,ultimate tensile strength,and elongation of 5 Ti/AZ91 composite are measured to be 212 MPa,323 MPa,and 10.1%,respectively.Microstructure analysis revealed that Ti particles are elongated along the extrusion direction,forming a discontinuous strip Ti particles,fine precipitated Mg_(17)Al_(12) phase inhibits dynamic recrystallization(DRX)behavior through Zener pinning effect and hinders the growth of matrix grains,resulting in refiner grains of 5 Ti/AZ91 composite.Heterogeneous deformed Ti particles and magnesium(Mg)matrix to generate additional heterogeneous deformation-induced(HDI)strengthening.Heterogeneous deformation-induced strengthening mainly contributed to the increment of yield strength for 5 Ti/AZ91 composite.