The impact properties of two selected metallocene-catalyzed ethylene-butene copolymers and one conventionalcopolymer were evaluated using Izod impact test. It is found that the metallocene-catalyzed copolymer shows su...The impact properties of two selected metallocene-catalyzed ethylene-butene copolymers and one conventionalcopolymer were evaluated using Izod impact test. It is found that the metallocene-catalyzed copolymer shows superior impactproperties. This result was explained on the basis of the more homogeneous inter-molecular composition distribution andnarrower molecular weight distribution, which leads to more homogeneous morphology with fewer defects. Stepwisecrystallization improves the impact properties, especially in the crack propagation process, to a large extent. This is due to thedecrease of entanglements by stepwise crystallization, which is advantageous for the chain slip and shear. The polymer withheterogeneous intra-molecular composition distribution exhibits a more evident improvement of impact properties understepwise crystallization.展开更多
Four polymers containing five-membered rings in the main chain, with or without conjugation structure along the backbone and with or without conjugated pendent groups, were designed and synthesized by metathesis cyclo...Four polymers containing five-membered rings in the main chain, with or without conjugation structure along the backbone and with or without conjugated pendent groups, were designed and synthesized by metathesis cyclopolymerization of functionalized α,ω-diynes, and cyclopolymerization of functionalized α,ω-dienes catalyzed by the α-diimine palladium-based catalyst, respectively. High to moderate monomer conversions were achieved. Chain structure, molecular weight, and molecular weight distribution(MWD) of the cyclopolymerization products were characterized by ~1 H-, ^(13) C-NMR, FTIR, and GPC. The polymers showed regular main chain structures,moderately high molecular weight, and narrow MWD. Thermal properties and chain stacking behaviors of the polymers were investigated by differential scanning calorimetry(DSC) and X-ray diffraction(XRD) as well as atomic force microscopy(AFM). The polymer with conjugation system in both the backbone and the pendent groups exhibited UV-Vis absorption at a much longer wavelength than those with the conjugation only in the backbone or only in the side groups. The polymers with conjugated backbone need more space for chain stacking, and the conjugated backbone causes enhanced size of polymer particles assembled from solution. The results showed that primary microstructures of the polymer exerted significant influences on the physical properties.展开更多
基金This work was supported by National Natural Science Foundation of China (No. 59703002).
文摘The impact properties of two selected metallocene-catalyzed ethylene-butene copolymers and one conventionalcopolymer were evaluated using Izod impact test. It is found that the metallocene-catalyzed copolymer shows superior impactproperties. This result was explained on the basis of the more homogeneous inter-molecular composition distribution andnarrower molecular weight distribution, which leads to more homogeneous morphology with fewer defects. Stepwisecrystallization improves the impact properties, especially in the crack propagation process, to a large extent. This is due to thedecrease of entanglements by stepwise crystallization, which is advantageous for the chain slip and shear. The polymer withheterogeneous intra-molecular composition distribution exhibits a more evident improvement of impact properties understepwise crystallization.
基金Financial support by the National Natural Science Foundation of China(No.51773178)
文摘Four polymers containing five-membered rings in the main chain, with or without conjugation structure along the backbone and with or without conjugated pendent groups, were designed and synthesized by metathesis cyclopolymerization of functionalized α,ω-diynes, and cyclopolymerization of functionalized α,ω-dienes catalyzed by the α-diimine palladium-based catalyst, respectively. High to moderate monomer conversions were achieved. Chain structure, molecular weight, and molecular weight distribution(MWD) of the cyclopolymerization products were characterized by ~1 H-, ^(13) C-NMR, FTIR, and GPC. The polymers showed regular main chain structures,moderately high molecular weight, and narrow MWD. Thermal properties and chain stacking behaviors of the polymers were investigated by differential scanning calorimetry(DSC) and X-ray diffraction(XRD) as well as atomic force microscopy(AFM). The polymer with conjugation system in both the backbone and the pendent groups exhibited UV-Vis absorption at a much longer wavelength than those with the conjugation only in the backbone or only in the side groups. The polymers with conjugated backbone need more space for chain stacking, and the conjugated backbone causes enhanced size of polymer particles assembled from solution. The results showed that primary microstructures of the polymer exerted significant influences on the physical properties.