Novel yellow-emitting phosphors of Dy^(3+)-doped double perovskite Ca_(2)MgTeO_(6) were synthesized by using a conventional high-temperature solid-state reaction.The phase purity,particle morphology,size distribution,...Novel yellow-emitting phosphors of Dy^(3+)-doped double perovskite Ca_(2)MgTeO_(6) were synthesized by using a conventional high-temperature solid-state reaction.The phase purity,particle morphology,size distribution,elemental composition,luminescence properties,and luminescence decay curves of the resulting products were then analyzed in detail.The Ca_(2)MgTeO_(6):Dy^(3+),Na^(+) phosphors show three emission peaks after near-ultraviolet excitation at 350 nm,which correspond to ^(4)F_(9/2)→^(6)H_(11/2),^(4)F_(9/2)→^(6)H_(13/2),and ^(4)F_(9/2)→^(6)H_(13/2) transitions,respectively.Among them,the strongest peak is observed at 573 nm.The best doping content of Dy^(3+)in Ca_(2)MgTeO_(6):xDy^(3+),xNa^(+) phosphors is x=5 mol%.The calculated critical distance of energy transfer between Dy^(3+) ions is 1.6 nm.Luminescence quenching is confirmed to be due to dipole-dipole interactions among Dy^(3+) ions.The phosphors show excellent thermal stability with high activation energy(0.27 eV).The Commission Internationale de l’Eclairage(CIE) chromaticity coordinates of the Ca_(2)MgTeO_(6) Dy^(3+),Na^(+) phosphors are located in the yellow region.White light-emitting diodes(w-LEDs) were fabricated with a high color rendering index(R_(a)) of 88 and a good correlated color temperature(CCT) of 5440 K.All observed properties indicate that Ca_(2)MgTeO_(6):Dy^(3+),Na^(+) phosphors have potential applications in display and photonic devices.展开更多
基金Project supported by the Natural Science Foundation of Shaanxi Province(2018JM5055)Hunan Provincial Key Laboratory of Xiangnan Rare-Precious Metals Compounds and Applications(2019XGJSKFJJ01)+2 种基金the Construction Program of the Key Discipline in Hunan Provincethe Projects of the Education Department of Hunan Province(18A465)Science and Technology Plan Project of Chenzhou City(jsyf2017014)。
文摘Novel yellow-emitting phosphors of Dy^(3+)-doped double perovskite Ca_(2)MgTeO_(6) were synthesized by using a conventional high-temperature solid-state reaction.The phase purity,particle morphology,size distribution,elemental composition,luminescence properties,and luminescence decay curves of the resulting products were then analyzed in detail.The Ca_(2)MgTeO_(6):Dy^(3+),Na^(+) phosphors show three emission peaks after near-ultraviolet excitation at 350 nm,which correspond to ^(4)F_(9/2)→^(6)H_(11/2),^(4)F_(9/2)→^(6)H_(13/2),and ^(4)F_(9/2)→^(6)H_(13/2) transitions,respectively.Among them,the strongest peak is observed at 573 nm.The best doping content of Dy^(3+)in Ca_(2)MgTeO_(6):xDy^(3+),xNa^(+) phosphors is x=5 mol%.The calculated critical distance of energy transfer between Dy^(3+) ions is 1.6 nm.Luminescence quenching is confirmed to be due to dipole-dipole interactions among Dy^(3+) ions.The phosphors show excellent thermal stability with high activation energy(0.27 eV).The Commission Internationale de l’Eclairage(CIE) chromaticity coordinates of the Ca_(2)MgTeO_(6) Dy^(3+),Na^(+) phosphors are located in the yellow region.White light-emitting diodes(w-LEDs) were fabricated with a high color rendering index(R_(a)) of 88 and a good correlated color temperature(CCT) of 5440 K.All observed properties indicate that Ca_(2)MgTeO_(6):Dy^(3+),Na^(+) phosphors have potential applications in display and photonic devices.