Sintered NdFeB magnets have complex microstructure that makes them susceptible to corrosion in active environments.The current paper evaluated the anticorrosion characteristics of multilayer titanium nitride ceramic c...Sintered NdFeB magnets have complex microstructure that makes them susceptible to corrosion in active environments.The current paper evaluated the anticorrosion characteristics of multilayer titanium nitride ceramic coating applied through cathodic arc physical vapour deposition(CAPVD) for protection of sintered NdFeB permanent magnets.The performance of ceramic coating was compared to the electrodeposited nickel coating having a copper interlayer.Electrochemical impedance spectroscopy(EIS) and cyclic polar...展开更多
The effect of cold rolling and post-rolling heat treatment on the microstructural and electrochemical properties of the 316L stainless steel was investigated.Two-pass and four-pass cold-rolled stainless steel specimen...The effect of cold rolling and post-rolling heat treatment on the microstructural and electrochemical properties of the 316L stainless steel was investigated.Two-pass and four-pass cold-rolled stainless steel specimens were heat-treated by annealing at 900℃followed by quenching in water.During the cold rolling,the microstructure of the as-received specimen transformed from austenite to strain-inducedα′-martensite due to significant plastic deformation that also resulted in significant grain elongation(i.e.,~33%and 223%increases in the grain elongation after two and four rolling passes,respectively).The hardness of the heat-treated as-received specimen decreased from HV 190 to 146 due to the recovery and recrystallization of the austenite grain structure.The cyclic polarization scans of the as-rolled and heat-treated specimens were obtained in 0.9wt%NaCl solution.The pitting potential of the four-pass rolled specimen was significantly increased from 322.3 to 930.5 mV after post-rolling heat treatment.The beneficial effect of the heat treatment process was evident from~10-times-lower corrosion current density and two-orders-of-magnitude-lower passive current density of the heat-treated specimens compared with those of the as-rolled specimens.Similarly,appreciably lower corrosion rate(3.302×10^(−4)mm/a)and higher pitting resistance(1115.5 mV)were exhibited by the postrolled heat-treated specimens compared with the as-rolled 316L stainless steel specimens.展开更多
文摘Sintered NdFeB magnets have complex microstructure that makes them susceptible to corrosion in active environments.The current paper evaluated the anticorrosion characteristics of multilayer titanium nitride ceramic coating applied through cathodic arc physical vapour deposition(CAPVD) for protection of sintered NdFeB permanent magnets.The performance of ceramic coating was compared to the electrodeposited nickel coating having a copper interlayer.Electrochemical impedance spectroscopy(EIS) and cyclic polar...
文摘The effect of cold rolling and post-rolling heat treatment on the microstructural and electrochemical properties of the 316L stainless steel was investigated.Two-pass and four-pass cold-rolled stainless steel specimens were heat-treated by annealing at 900℃followed by quenching in water.During the cold rolling,the microstructure of the as-received specimen transformed from austenite to strain-inducedα′-martensite due to significant plastic deformation that also resulted in significant grain elongation(i.e.,~33%and 223%increases in the grain elongation after two and four rolling passes,respectively).The hardness of the heat-treated as-received specimen decreased from HV 190 to 146 due to the recovery and recrystallization of the austenite grain structure.The cyclic polarization scans of the as-rolled and heat-treated specimens were obtained in 0.9wt%NaCl solution.The pitting potential of the four-pass rolled specimen was significantly increased from 322.3 to 930.5 mV after post-rolling heat treatment.The beneficial effect of the heat treatment process was evident from~10-times-lower corrosion current density and two-orders-of-magnitude-lower passive current density of the heat-treated specimens compared with those of the as-rolled specimens.Similarly,appreciably lower corrosion rate(3.302×10^(−4)mm/a)and higher pitting resistance(1115.5 mV)were exhibited by the postrolled heat-treated specimens compared with the as-rolled 316L stainless steel specimens.