The void evolution inα-Al2O3 irradiated by En≥1 MeV neutrons of 3×10^(20)cm^(-2) and post-annealed from 100°C to 1050°C has been studied by a positron annihilation lifetime technique.The void nucleati...The void evolution inα-Al2O3 irradiated by En≥1 MeV neutrons of 3×10^(20)cm^(-2) and post-annealed from 100°C to 1050°C has been studied by a positron annihilation lifetime technique.The void nucleation starts at 500°C.In the annealing temperature region from 550℃ to 750℃,the radius of created voids keeps constant at a value of about 0.29 nm and the number of voids increases with increasing temperature.Afterwards,the radius of voids increases rapidly with the increasing annealing temperature and reaches 1.21nm at 1050℃.展开更多
The g-factors of the rotational states along the positive parity yrast band in even-even nuclei ^(84)Zr were measured up to a spin I=16^(+)by a transient magnetic field-ion implanted perturbed angular distribution met...The g-factors of the rotational states along the positive parity yrast band in even-even nuclei ^(84)Zr were measured up to a spin I=16^(+)by a transient magnetic field-ion implanted perturbed angular distribution method and calculated by a cranking shell model.A peak structure of the g-factors has been observed for the first time.The measured g-factors confirm the mixed configuration of proton and neutron alignments.展开更多
基金Supported in par t by the National Natural Science Foundation of China under Grant No.19835050the Nuclear Indus try Science Foundation of China under Grant No.H7196BO116the Contract of 97J11.2.8HZ010.
文摘The void evolution inα-Al2O3 irradiated by En≥1 MeV neutrons of 3×10^(20)cm^(-2) and post-annealed from 100°C to 1050°C has been studied by a positron annihilation lifetime technique.The void nucleation starts at 500°C.In the annealing temperature region from 550℃ to 750℃,the radius of created voids keeps constant at a value of about 0.29 nm and the number of voids increases with increasing temperature.Afterwards,the radius of voids increases rapidly with the increasing annealing temperature and reaches 1.21nm at 1050℃.
基金Supported by the National Natural Science Foundation of China under Grant No.19775070.
文摘The g-factors of the rotational states along the positive parity yrast band in even-even nuclei ^(84)Zr were measured up to a spin I=16^(+)by a transient magnetic field-ion implanted perturbed angular distribution method and calculated by a cranking shell model.A peak structure of the g-factors has been observed for the first time.The measured g-factors confirm the mixed configuration of proton and neutron alignments.