The phase composition, magnetic properties i.e. coercivity and the magnetic polarization at room temperature for the bulk Fe67Co5Nd3Y6B19 and Fe64Co5Nd6Y6B19 alloys were studied. The bulk amorphous Fe67CosNd3Y6B19 all...The phase composition, magnetic properties i.e. coercivity and the magnetic polarization at room temperature for the bulk Fe67Co5Nd3Y6B19 and Fe64Co5Nd6Y6B19 alloys were studied. The bulk amorphous Fe67CosNd3Y6B19 alloy, inhomogeneous in the as-quenched state, crystallized after annealing at 948 K for 0.5 h and consisted of Nd2Fe14B-type, Fe2B and paramagnetic phases. The rapidly solidified Fe64Co5Nd6Y6B19 alloy contained the Nd2Fel4B-type and paramagnetic phases. The annealing of the bulk Fe67CosNd3Y6B19 alloy at 948 K for 0.5 h led to hard magnetic properties. However, the bulk Fe64Co5Nd6Y6B19 alloy exhibited good hard magnetic properties directly after preparation.展开更多
基金supported by the grants PBZ-MEiN/01/2006/09 (M. Hasiak)PBZ-KBN-115/T08/04 (J. Kaleta)
文摘The phase composition, magnetic properties i.e. coercivity and the magnetic polarization at room temperature for the bulk Fe67Co5Nd3Y6B19 and Fe64Co5Nd6Y6B19 alloys were studied. The bulk amorphous Fe67CosNd3Y6B19 alloy, inhomogeneous in the as-quenched state, crystallized after annealing at 948 K for 0.5 h and consisted of Nd2Fe14B-type, Fe2B and paramagnetic phases. The rapidly solidified Fe64Co5Nd6Y6B19 alloy contained the Nd2Fel4B-type and paramagnetic phases. The annealing of the bulk Fe67CosNd3Y6B19 alloy at 948 K for 0.5 h led to hard magnetic properties. However, the bulk Fe64Co5Nd6Y6B19 alloy exhibited good hard magnetic properties directly after preparation.