To improve the sliding wear resistance of AZ91D magnesium alloy, Cu-based amorphous composite coatings made of CuaTTi34Zr11Nis and Cu47Ti34Zr11Ni8+20 wt pct SiC powders were fabricated on AZ91D magnesium alloy by las...To improve the sliding wear resistance of AZ91D magnesium alloy, Cu-based amorphous composite coatings made of CuaTTi34Zr11Nis and Cu47Ti34Zr11Ni8+20 wt pct SiC powders were fabricated on AZ91D magnesium alloy by laser cladding, respectively. SEM (scanning electron microscopy), EDS (energy dispersive X-ray spectroscopy), XRD (X-ray diffraction) and TEM (transmission electron microscopy) techniques were employed to study the phases of the coatings. The results show that the coatings mainly consist of amorphous phase and different intermetallic compounds. The reason of formation of amorphous phase and the function of SiC particles were explained in details.展开更多
Laser cladding technique has been applied to renovate some partially-damaged (or worn) components with Fe, Ni, Co-base alloys, hence to improve their hardness values and wear resistance successfully in previous report...Laser cladding technique has been applied to renovate some partially-damaged (or worn) components with Fe, Ni, Co-base alloys, hence to improve their hardness values and wear resistance successfully in previous reports. But for some punching or shearing cast iron dies damaged or worn in automobile manufacture, the renovated surfaces also bear some impact loading. Therefore, a small-energy and multi-impact (SEMI) test was designed to investigate the fracture behaviour of renovated cast iron dies achieved by laser cladding of Fe and Ni-base alloys under SEMI loading to meet above requirement. observations show that the fracture took place in the substrate near to the substrate/coating interface rather than at the interface. The tempering temperature has a great influence on the cycles to fracture of laser-clad samples under SEMl loading, i.e. the low tempering temperature of 300℃ gives a maximum cycle to fracture, while a higher tempering temperature of 400℃ has a minimum. Furthermore, the fracture mechanism has also been discussed in present study展开更多
The microstructure and wear behaviour of the thermite reaction coating produced by the hybrid laser claddingremelting on AA7075 aluminum alloy for the systems of Al-CuO-SiO2, Al-Cr2O3-SiO2, Al-Fe2O3-SiO2, and Al-TiO2-...The microstructure and wear behaviour of the thermite reaction coating produced by the hybrid laser claddingremelting on AA7075 aluminum alloy for the systems of Al-CuO-SiO2, Al-Cr2O3-SiO2, Al-Fe2O3-SiO2, and Al-TiO2-SiO2 were studied. The results of the X-ray diffraction (XRD) analysis show that in all the four reaction coatings, α-Al2O3 and γ-Al2O3 phases were present at the top surface, together with various intermetallic phases, the corresponding reduced metal and Al phase in the fusion zone. Under the dry sliding condition, the wear resistance, in terms of weight loss, of the laser-clad specimens was considerably higher than that of the untreated specimen. The predominant wear mechanism of the former specimens was abrasive wear, while for the latter, it was the adhesive wear that prevailed.展开更多
基金supported by the Open Fund of the State Key Laboratory of Advanced Welding Production Technology in Harbin Institute of Technology,Chinathe Open Fund of the State Key Laboratory of Materials Processing and Die&Mould Technology in Huazhong University of Science and Technology,China
文摘To improve the sliding wear resistance of AZ91D magnesium alloy, Cu-based amorphous composite coatings made of CuaTTi34Zr11Nis and Cu47Ti34Zr11Ni8+20 wt pct SiC powders were fabricated on AZ91D magnesium alloy by laser cladding, respectively. SEM (scanning electron microscopy), EDS (energy dispersive X-ray spectroscopy), XRD (X-ray diffraction) and TEM (transmission electron microscopy) techniques were employed to study the phases of the coatings. The results show that the coatings mainly consist of amorphous phase and different intermetallic compounds. The reason of formation of amorphous phase and the function of SiC particles were explained in details.
文摘Laser cladding technique has been applied to renovate some partially-damaged (or worn) components with Fe, Ni, Co-base alloys, hence to improve their hardness values and wear resistance successfully in previous reports. But for some punching or shearing cast iron dies damaged or worn in automobile manufacture, the renovated surfaces also bear some impact loading. Therefore, a small-energy and multi-impact (SEMI) test was designed to investigate the fracture behaviour of renovated cast iron dies achieved by laser cladding of Fe and Ni-base alloys under SEMI loading to meet above requirement. observations show that the fracture took place in the substrate near to the substrate/coating interface rather than at the interface. The tempering temperature has a great influence on the cycles to fracture of laser-clad samples under SEMl loading, i.e. the low tempering temperature of 300℃ gives a maximum cycle to fracture, while a higher tempering temperature of 400℃ has a minimum. Furthermore, the fracture mechanism has also been discussed in present study
文摘The microstructure and wear behaviour of the thermite reaction coating produced by the hybrid laser claddingremelting on AA7075 aluminum alloy for the systems of Al-CuO-SiO2, Al-Cr2O3-SiO2, Al-Fe2O3-SiO2, and Al-TiO2-SiO2 were studied. The results of the X-ray diffraction (XRD) analysis show that in all the four reaction coatings, α-Al2O3 and γ-Al2O3 phases were present at the top surface, together with various intermetallic phases, the corresponding reduced metal and Al phase in the fusion zone. Under the dry sliding condition, the wear resistance, in terms of weight loss, of the laser-clad specimens was considerably higher than that of the untreated specimen. The predominant wear mechanism of the former specimens was abrasive wear, while for the latter, it was the adhesive wear that prevailed.