The microstructure and mechanical behaviors of NiAl-28Cr-5Mo-1Nb eutectic alloy were investigated by using scanning electron microscopy, X-ray diffraction, transmission electron microscopy and compression tests, respe...The microstructure and mechanical behaviors of NiAl-28Cr-5Mo-1Nb eutectic alloy were investigated by using scanning electron microscopy, X-ray diffraction, transmission electron microscopy and compression tests, respectively. The alloy is mainly composed of three phases, which are the gray lamellar Cr（Mo） plate, black NiAI matrix and semicontinuously distributed Cr2Nb-type Laves phase. Through Nb addition, NiAl-Cr（Mo）/Nb alloy exhibits a reasonable balance of high temperature strength and room temperature compression ductility and its mechanical behaviors are superior to the NiAl-28Cr-6Mo eutectic alloy at all temperature. The elevated temperature compression deformation behavior of NiAl-Cr（Mo）/Nb alloy can be properly described by power-law equation.the National High Technology Committee of China （No. 863-715-005-0030） for financial supports.展开更多
Effect of 0.1 wt pct Dy addition on microstructure and compressive behavior of NiAl-28Cr-5.8Mo-0.2 Hf eutectic alloy was investigated. The results showed that remarkable lamellar refinement can be achieved with the ad...Effect of 0.1 wt pct Dy addition on microstructure and compressive behavior of NiAl-28Cr-5.8Mo-0.2 Hf eutectic alloy was investigated. The results showed that remarkable lamellar refinement can be achieved with the addition of 0.1 wt pct Dy. The Dy addition results in the decrease in Young＇s modulus of alloy and the.enhancement of the compressive strength and ductility of alloy at all testing temperatures. The lamellar refinement, the increased dislocation networks located at the interfaces of NiAl/Cr（Mo） and the strengthening of cell boundary are benefical to the improvement of compressive properties of the alloy.展开更多
基金The authors would like to acknowledge the National Natural Science Foundation of China(No.59895152)the National High Technology Committee of China(No.863-715-005-0030)for financial supports.
文摘The microstructure and mechanical behaviors of NiAl-28Cr-5Mo-1Nb eutectic alloy were investigated by using scanning electron microscopy, X-ray diffraction, transmission electron microscopy and compression tests, respectively. The alloy is mainly composed of three phases, which are the gray lamellar Cr（Mo） plate, black NiAI matrix and semicontinuously distributed Cr2Nb-type Laves phase. Through Nb addition, NiAl-Cr（Mo）/Nb alloy exhibits a reasonable balance of high temperature strength and room temperature compression ductility and its mechanical behaviors are superior to the NiAl-28Cr-6Mo eutectic alloy at all temperature. The elevated temperature compression deformation behavior of NiAl-Cr（Mo）/Nb alloy can be properly described by power-law equation.the National High Technology Committee of China （No. 863-715-005-0030） for financial supports.
基金The authors would like to thank the National Natural Science Foundation of China for the financial support under contract No.59895152the National High Technology Committee of China under contract No.863-715-005-0030.
文摘Effect of 0.1 wt pct Dy addition on microstructure and compressive behavior of NiAl-28Cr-5.8Mo-0.2 Hf eutectic alloy was investigated. The results showed that remarkable lamellar refinement can be achieved with the addition of 0.1 wt pct Dy. The Dy addition results in the decrease in Young＇s modulus of alloy and the.enhancement of the compressive strength and ductility of alloy at all testing temperatures. The lamellar refinement, the increased dislocation networks located at the interfaces of NiAl/Cr（Mo） and the strengthening of cell boundary are benefical to the improvement of compressive properties of the alloy.