Na0.5Li0.5Zr2(PO4)3has been synthesized by solid state reaction and characterized by thermogravimetry/ differential thermal analyses (TGA/DTA) in the temperature range 300 - 1573 K. X-ray diffraction measure- ments ha...Na0.5Li0.5Zr2(PO4)3has been synthesized by solid state reaction and characterized by thermogravimetry/ differential thermal analyses (TGA/DTA) in the temperature range 300 - 1573 K. X-ray diffraction measure- ments have been carried out to determine the phase of the composition and scanning electron microscopy (SEM) for microstructure evaluation. Impedance spectroscopy at different temperatures (310 - 600 K) and frequencies (300 kHz - 1 GHz) have been carried out and the dielectric relaxation behaviour was determined under the same conditions. A dc conductivity maximum value of 0.25 S/m at 580 K was observed. However, the mixed alkali effect was not observed. The material exhibited relaxation behaviour with a peak in the dielectric permitivity at 469 K. There were no structural transformations observed.展开更多
Natural dyes from flame tree flower, Pawpaw leaf and their mixtures were used as sensitizers to fabricate dye-sensitized solar cells (DSSC). The photoelectrochemical performance of the Flame tree flower dye extract sh...Natural dyes from flame tree flower, Pawpaw leaf and their mixtures were used as sensitizers to fabricate dye-sensitized solar cells (DSSC). The photoelectrochemical performance of the Flame tree flower dye extract showed an open-circuit voltage (VOC) of 0.50 V, short-circuit current density (JSC) of 0.668 mA/cm2, a fill factor (FF) of 0.588 and a conversion efficiency of 0.20%. The conversion efficiency of the DSSCs prepared by pawpaw leaf extract was 0.20%, with VOC of 0.50 V;short-circuit current density, JSC of 0.649 mA/cm2 and FF of 0.605. The conversion efficiency for the flame tree flower and pawpaw leaf dye mixture was 0.27%, with VOC of 0.518 V, JSC of 0.744 mA/cm2 and FF of 0.69. Although the conversion efficiencies, Jsc and the Voc of the prepared dye cells were lower than the respective 1.185%, 7.49 mA/cm2 and 0.64V reported for ruthenium, their fill factors (FF) were higher than that of ruthenium (0.497). It was also observed that both the short-circuit current density and the fill factors of the cells were enhanced using mixed dye.展开更多
Cadmium Zinc Sulfide, Cd1-xZnxS thin films were deposited by chemical bath deposition technique at bath temperature of 75°C. The morphology of the films was analyzed by scanning electron microscope, the optical c...Cadmium Zinc Sulfide, Cd1-xZnxS thin films were deposited by chemical bath deposition technique at bath temperature of 75°C. The morphology of the films was analyzed by scanning electron microscope, the optical constants of the films were estimated from the transmission and reflection spectra of the films in the wavelength range of 300 - 900 nm. The films had a transmittance between 75% and 85% and optical band gap in the range 2.8 - 3.4 eV. The dependence of the refractive index of the films on the wavelength was investigated using the single oscillator model, from which the dispersion parameters were determined. The high frequency dielectric constant εL and the ratio of the carrier concentration to the effective mass N/m* were estimated based on the Spitzer and Fan model. Both εL and N/m* show a decrease in value with increase in Zinc content.展开更多
文摘Na0.5Li0.5Zr2(PO4)3has been synthesized by solid state reaction and characterized by thermogravimetry/ differential thermal analyses (TGA/DTA) in the temperature range 300 - 1573 K. X-ray diffraction measure- ments have been carried out to determine the phase of the composition and scanning electron microscopy (SEM) for microstructure evaluation. Impedance spectroscopy at different temperatures (310 - 600 K) and frequencies (300 kHz - 1 GHz) have been carried out and the dielectric relaxation behaviour was determined under the same conditions. A dc conductivity maximum value of 0.25 S/m at 580 K was observed. However, the mixed alkali effect was not observed. The material exhibited relaxation behaviour with a peak in the dielectric permitivity at 469 K. There were no structural transformations observed.
文摘Natural dyes from flame tree flower, Pawpaw leaf and their mixtures were used as sensitizers to fabricate dye-sensitized solar cells (DSSC). The photoelectrochemical performance of the Flame tree flower dye extract showed an open-circuit voltage (VOC) of 0.50 V, short-circuit current density (JSC) of 0.668 mA/cm2, a fill factor (FF) of 0.588 and a conversion efficiency of 0.20%. The conversion efficiency of the DSSCs prepared by pawpaw leaf extract was 0.20%, with VOC of 0.50 V;short-circuit current density, JSC of 0.649 mA/cm2 and FF of 0.605. The conversion efficiency for the flame tree flower and pawpaw leaf dye mixture was 0.27%, with VOC of 0.518 V, JSC of 0.744 mA/cm2 and FF of 0.69. Although the conversion efficiencies, Jsc and the Voc of the prepared dye cells were lower than the respective 1.185%, 7.49 mA/cm2 and 0.64V reported for ruthenium, their fill factors (FF) were higher than that of ruthenium (0.497). It was also observed that both the short-circuit current density and the fill factors of the cells were enhanced using mixed dye.
文摘Cadmium Zinc Sulfide, Cd1-xZnxS thin films were deposited by chemical bath deposition technique at bath temperature of 75°C. The morphology of the films was analyzed by scanning electron microscope, the optical constants of the films were estimated from the transmission and reflection spectra of the films in the wavelength range of 300 - 900 nm. The films had a transmittance between 75% and 85% and optical band gap in the range 2.8 - 3.4 eV. The dependence of the refractive index of the films on the wavelength was investigated using the single oscillator model, from which the dispersion parameters were determined. The high frequency dielectric constant εL and the ratio of the carrier concentration to the effective mass N/m* were estimated based on the Spitzer and Fan model. Both εL and N/m* show a decrease in value with increase in Zinc content.