The hot deformation behavior of an as-cast OCrl7Mnl4Mo2N duplex stainless steel has been studied by hot compression test at the temperature range from 1000℃ to 1200℃, and the strain rates are 0.1 s-1, 1 s-1 and 5 s-...The hot deformation behavior of an as-cast OCrl7Mnl4Mo2N duplex stainless steel has been studied by hot compression test at the temperature range from 1000℃ to 1200℃, and the strain rates are 0.1 s-1, 1 s-1 and 5 s-1, respectively. It was found that during hot deformation there is only dynamic recovery taking place within the δ-ferrite phase, but the γ-austenite phase undergoes dynamic recrystallization. The activation energy of the steel for hot compression is estimated to be 480 kJ/mol.展开更多
Acicular ferrite microstructure was achieved for an ultralow carbon pipeline steel through the improved thermome chanical control process (TMCP), which was based on the transformation process of deformed austenite of ...Acicular ferrite microstructure was achieved for an ultralow carbon pipeline steel through the improved thermome chanical control process (TMCP), which was based on the transformation process of deformed austenite of steel. Compared with commercial pipeline steels, the experimental ultralow carbon pipeline steel possessed the satisfied strength and toughness behaviors under the current improved TMCP, although it contained only approximately 0.025% C, vvhich should mainly be attributed to the microstructural characteristics of acicular ferrite.展开更多
文摘The hot deformation behavior of an as-cast OCrl7Mnl4Mo2N duplex stainless steel has been studied by hot compression test at the temperature range from 1000℃ to 1200℃, and the strain rates are 0.1 s-1, 1 s-1 and 5 s-1, respectively. It was found that during hot deformation there is only dynamic recovery taking place within the δ-ferrite phase, but the γ-austenite phase undergoes dynamic recrystallization. The activation energy of the steel for hot compression is estimated to be 480 kJ/mol.
基金The present work was financially supported by a China National‘973’Project No.G1998061511the Natural Science Fund of Hebei Province No.501205.
文摘Acicular ferrite microstructure was achieved for an ultralow carbon pipeline steel through the improved thermome chanical control process (TMCP), which was based on the transformation process of deformed austenite of steel. Compared with commercial pipeline steels, the experimental ultralow carbon pipeline steel possessed the satisfied strength and toughness behaviors under the current improved TMCP, although it contained only approximately 0.025% C, vvhich should mainly be attributed to the microstructural characteristics of acicular ferrite.