In this study, it was examined whether the dynamics of polymer chains at a surface is different from that in thebulk, and if so, to what extent they differ in terms of surface glass transition temperature and diffusio...In this study, it was examined whether the dynamics of polymer chains at a surface is different from that in thebulk, and if so, to what extent they differ in terms of surface glass transition temperature and diffusion coefficient. Obtainedresults clearly indicate that surface chains can travel for a relatively large distance in comparison with the characteristiclength scale of usual segmental motion even at a temperature below its bulk glass transition temperature, T_g^b. This isconsistent with our previous results that the surface glass transition temperature is much lower than the corresponding T_g^b.Also, it was experimentally revealed that there was a gradient of molecular motion in the surface region.展开更多
Surface molecular motions of amorphous polymeric solids have been directly measured on the basis of scanningviscoelasticity microscopic (SVM) and lateral force microscopic (LFM) measurements. SVM and LFM measurements ...Surface molecular motions of amorphous polymeric solids have been directly measured on the basis of scanningviscoelasticity microscopic (SVM) and lateral force microscopic (LFM) measurements. SVM and LFM measurements werecarried out for films of conventional monodisperse polystyrene (PS) with sec-butyl and proton-terminated end groups atroom temperature. In the case of the number-average molecular weight, M_n, less than ca. 4.0×10~4, the surface was in a glass-rubber transition state even though the bulk glass transition temperature, T_g was far above room temperature, meaning thatthe surface molecular motion was fairly active compared with that in the bulk. LFM measurements of the, monodisperse PSfilms at various scanning rates and temperatures revealed that the time-temperature superposition was applicable to thesurface mechanical relaxation behavior and also that the surface glass transition temperature, T_g~σ, was depressed incomparison with the bulk one even though the magnitude of M_n was fairly high at 1.40×10~5. The surface molecular motionof monodisperse PS with various chain end groups was investigated on the basis of temperature-dependent scanningviscoelasticity microscopy (TDSVM). The T_g~σs for the PS films with M_n of 4.9×10~6 to 1.45×10~6 measured by TDSVMwere smaller than those for the bulk one, with corresponding M_ns, and the T_g~σs for M_ns smaller than ca. 4.0×10~4 were lowerthan room temperature (293 K). The active thermal molecular motion at the polymeric solid surface can be interpreted interms of an excess free volume near the surface region induced by the surface localization of chain end groups. In the case ofM_n=ca. 5.0×10~4, the T_g~σs for the α, ω-diamino-terminated PS (α,ω-PS(NH_2)_2) and α, ω-dicarboxy-terminated PS (α, ω-PS(COOH)_2) films were higher than that of the PS film. The change of T_g~σ for the PS film with various chain end groups canbe explained in terms of the depth distribution of chain end groups at the surface region depending on the relativehydrophobicity.展开更多
基金This work was in part supported by a Gran-in-Aid for Scientific Research (A)(#13355034) from the Ministry of Education, Science, Sports, and Culture, Japan.
文摘In this study, it was examined whether the dynamics of polymer chains at a surface is different from that in thebulk, and if so, to what extent they differ in terms of surface glass transition temperature and diffusion coefficient. Obtainedresults clearly indicate that surface chains can travel for a relatively large distance in comparison with the characteristiclength scale of usual segmental motion even at a temperature below its bulk glass transition temperature, T_g^b. This isconsistent with our previous results that the surface glass transition temperature is much lower than the corresponding T_g^b.Also, it was experimentally revealed that there was a gradient of molecular motion in the surface region.
文摘Surface molecular motions of amorphous polymeric solids have been directly measured on the basis of scanningviscoelasticity microscopic (SVM) and lateral force microscopic (LFM) measurements. SVM and LFM measurements werecarried out for films of conventional monodisperse polystyrene (PS) with sec-butyl and proton-terminated end groups atroom temperature. In the case of the number-average molecular weight, M_n, less than ca. 4.0×10~4, the surface was in a glass-rubber transition state even though the bulk glass transition temperature, T_g was far above room temperature, meaning thatthe surface molecular motion was fairly active compared with that in the bulk. LFM measurements of the, monodisperse PSfilms at various scanning rates and temperatures revealed that the time-temperature superposition was applicable to thesurface mechanical relaxation behavior and also that the surface glass transition temperature, T_g~σ, was depressed incomparison with the bulk one even though the magnitude of M_n was fairly high at 1.40×10~5. The surface molecular motionof monodisperse PS with various chain end groups was investigated on the basis of temperature-dependent scanningviscoelasticity microscopy (TDSVM). The T_g~σs for the PS films with M_n of 4.9×10~6 to 1.45×10~6 measured by TDSVMwere smaller than those for the bulk one, with corresponding M_ns, and the T_g~σs for M_ns smaller than ca. 4.0×10~4 were lowerthan room temperature (293 K). The active thermal molecular motion at the polymeric solid surface can be interpreted interms of an excess free volume near the surface region induced by the surface localization of chain end groups. In the case ofM_n=ca. 5.0×10~4, the T_g~σs for the α, ω-diamino-terminated PS (α,ω-PS(NH_2)_2) and α, ω-dicarboxy-terminated PS (α, ω-PS(COOH)_2) films were higher than that of the PS film. The change of T_g~σ for the PS film with various chain end groups canbe explained in terms of the depth distribution of chain end groups at the surface region depending on the relativehydrophobicity.