An a-C/a-C:N junction,which used palmyra sugar as the carbon source and ammonium hydroxide(NH4OH)as the dopant source,was successfully deposited on the ITO glass substrate using the nano-spraying method.The current-vo...An a-C/a-C:N junction,which used palmyra sugar as the carbon source and ammonium hydroxide(NH4OH)as the dopant source,was successfully deposited on the ITO glass substrate using the nano-spraying method.The current-voltage relationship of the junction was found to be a Schottky-like contact,and therefore the junction shows the characteristic rectifiers.This means the a-C and a-C:N are semiconductors with different types of conduction.Moreover,the samples showed an increase in current and voltage value when exposed to visible light(bright state)compared to the dark condition,thereby,indicating the creation of electron-hole pairs during the exposure.It was also discovered that the relationship between current and voltage for the a-C/a-C:N junction sample formed a curve that satisfies the rule of the photovoltaic effect when exposed to visible light from a light bulb.The exposure of this sample to direct sunlight at AM 1.5 conditions produced a curve that meets the rules for the emergence of the photovoltaic effect with higher characteristics for the current-voltage relationship.Thus,the a-C/a-C:N junction sample is a solar cell successfully fabricated using a sample method and has a maximum efficiency of 0.0013%.展开更多
基金funded by the University of Muhammadiyah Malang through a doctoral scientific work development program and also by theMinistry of Finance of Indonesia through the LPDP BUDI-DN scholarship(BP),and National Competitive Fundamental Research Grant(Hibah Penelitian Dasar),Kemendikbudristek,2021–2022(D).
文摘An a-C/a-C:N junction,which used palmyra sugar as the carbon source and ammonium hydroxide(NH4OH)as the dopant source,was successfully deposited on the ITO glass substrate using the nano-spraying method.The current-voltage relationship of the junction was found to be a Schottky-like contact,and therefore the junction shows the characteristic rectifiers.This means the a-C and a-C:N are semiconductors with different types of conduction.Moreover,the samples showed an increase in current and voltage value when exposed to visible light(bright state)compared to the dark condition,thereby,indicating the creation of electron-hole pairs during the exposure.It was also discovered that the relationship between current and voltage for the a-C/a-C:N junction sample formed a curve that satisfies the rule of the photovoltaic effect when exposed to visible light from a light bulb.The exposure of this sample to direct sunlight at AM 1.5 conditions produced a curve that meets the rules for the emergence of the photovoltaic effect with higher characteristics for the current-voltage relationship.Thus,the a-C/a-C:N junction sample is a solar cell successfully fabricated using a sample method and has a maximum efficiency of 0.0013%.