Taking a Ti−5Al−5Mo−5V−1Cr−1Fe alloy as exemplary case,the fatigue crack growth sensitivity and fracture features with various tailoredαphase morphologies were thoroughly investigated using fatigue crack growth rate(...Taking a Ti−5Al−5Mo−5V−1Cr−1Fe alloy as exemplary case,the fatigue crack growth sensitivity and fracture features with various tailoredαphase morphologies were thoroughly investigated using fatigue crack growth rate(FCGR)test,optical microscopy(OM)and scanning electron microscopy(SEM).The tailored microstructures by heat treatments include the fine and coarse secondaryαphase,as well as the widmanstatten and basket weave features.The sample with coarse secondaryαphase exhibits better comprehensive properties of good crack propagation resistance(with long Paris regime ranging from 15 to 60 MPa·m1/2),high yield strength(1113 MPa)and ultimate strength(1150 MPa),and good elongation(11.6%).The good crack propagation resistance can be attributed to crack deflection,long secondary crack,and tortuous crack path induced by coarse secondaryαphase.展开更多
基金Project(U1867201)supported by the National Natural Science Foundation of ChinaProject supported by State Key Laboratory of Powder Metallurgy,Central South University,China。
文摘Taking a Ti−5Al−5Mo−5V−1Cr−1Fe alloy as exemplary case,the fatigue crack growth sensitivity and fracture features with various tailoredαphase morphologies were thoroughly investigated using fatigue crack growth rate(FCGR)test,optical microscopy(OM)and scanning electron microscopy(SEM).The tailored microstructures by heat treatments include the fine and coarse secondaryαphase,as well as the widmanstatten and basket weave features.The sample with coarse secondaryαphase exhibits better comprehensive properties of good crack propagation resistance(with long Paris regime ranging from 15 to 60 MPa·m1/2),high yield strength(1113 MPa)and ultimate strength(1150 MPa),and good elongation(11.6%).The good crack propagation resistance can be attributed to crack deflection,long secondary crack,and tortuous crack path induced by coarse secondaryαphase.