The low voltage pulsed magnetic field(LVPMF)disrupts the columnar dendrite growth,and the columnarto-equiaxed transition(CET)occurs during the directional solidification of superalloy K4169.Within the pulse voltage ra...The low voltage pulsed magnetic field(LVPMF)disrupts the columnar dendrite growth,and the columnarto-equiaxed transition(CET)occurs during the directional solidification of superalloy K4169.Within the pulse voltage ranging from 100Vto 200 V,a transition from columnar to equiaxed grain was observed,and the grain size decreased as the pulse voltage rised.As the pulse frequency increased,the CET occurred,and the grains were refined.However,the grains became coarse,and the solidification structure was columnar crystal again when frequency increased to 10 Hz.The LVPMF had an optimal frequency to promote CET.The LVPMF on the CET was affected by the withdrawal speed and increasing the withdrawal speed enhances the CET.The distribution of electromagnetic force and flow field in the melt under the LVPMF were modeled and simulated to reveal the CET mechanism.It is considered that the CET should be attributed to the coupling effects of magnetic vibration and melt convection induced by the LVPMF.展开更多
The effect of the pulsed magnetic field on the grain refinement of superalloy K4169 has been studied in directional solidification.In the presence of the solid-liquid interface condition,the distributions of the elect...The effect of the pulsed magnetic field on the grain refinement of superalloy K4169 has been studied in directional solidification.In the presence of the solid-liquid interface condition,the distributions of the electromagnetic force,flow field,temperature field,and Joule heat in front of the solid-liquid interface in directional solidification with the pulsed magnetic field are simulated.The calculation results show that the largest electromagnetic force in the melt appears near the solid-liquid interface,and the electromagnetic force is distributed in a gradient.There are intensive electromagnetic vibrations in front of the solid-liquid interface.The forced melt convection is mainly concentrated in front of the solid-liquid interface,accompanied by a larger flow velocity.The simulation results indicate that the grain refinement is attributed to that the electromagnetic vibration and forced convection increase the nucleation rate and the probability of dendrite fragments survival,for making dendrite easily fragmented,homogenizing the melt temperature,and increasing the undercooling in front of the solid-liquid interface.展开更多
基金supported by the National Natural Science Foundation of China(No.51674236)the Key Research and Development Program of Liaoning Province(2019JH2/10100009)+1 种基金the National Science and Technology Major Project(No.2017-VI-00-0073)the National Key Research and Development Program(No.2018YFA0702900).
文摘The low voltage pulsed magnetic field(LVPMF)disrupts the columnar dendrite growth,and the columnarto-equiaxed transition(CET)occurs during the directional solidification of superalloy K4169.Within the pulse voltage ranging from 100Vto 200 V,a transition from columnar to equiaxed grain was observed,and the grain size decreased as the pulse voltage rised.As the pulse frequency increased,the CET occurred,and the grains were refined.However,the grains became coarse,and the solidification structure was columnar crystal again when frequency increased to 10 Hz.The LVPMF had an optimal frequency to promote CET.The LVPMF on the CET was affected by the withdrawal speed and increasing the withdrawal speed enhances the CET.The distribution of electromagnetic force and flow field in the melt under the LVPMF were modeled and simulated to reveal the CET mechanism.It is considered that the CET should be attributed to the coupling effects of magnetic vibration and melt convection induced by the LVPMF.
基金financially supported by the National Natural Science Foundation of China (No. 51674236)the Key Research and Development Program of Liaoning Province (No.2019JH2/10100009)+1 种基金the National Science and Technology Major Project (No.2017-Ⅵ-0003-0073)the National Key Research and Development Program (No.2018Y-FA0702900)。
文摘The effect of the pulsed magnetic field on the grain refinement of superalloy K4169 has been studied in directional solidification.In the presence of the solid-liquid interface condition,the distributions of the electromagnetic force,flow field,temperature field,and Joule heat in front of the solid-liquid interface in directional solidification with the pulsed magnetic field are simulated.The calculation results show that the largest electromagnetic force in the melt appears near the solid-liquid interface,and the electromagnetic force is distributed in a gradient.There are intensive electromagnetic vibrations in front of the solid-liquid interface.The forced melt convection is mainly concentrated in front of the solid-liquid interface,accompanied by a larger flow velocity.The simulation results indicate that the grain refinement is attributed to that the electromagnetic vibration and forced convection increase the nucleation rate and the probability of dendrite fragments survival,for making dendrite easily fragmented,homogenizing the melt temperature,and increasing the undercooling in front of the solid-liquid interface.