To improve the visible light absorption and photocatalytic activity of titanium dioxide nanotube arrays(TONTAs), ZnFe_2O_4(ZFO) nanocrystals were perfused into pristine TONTA pipelines using a novel bias voltageassist...To improve the visible light absorption and photocatalytic activity of titanium dioxide nanotube arrays(TONTAs), ZnFe_2O_4(ZFO) nanocrystals were perfused into pristine TONTA pipelines using a novel bias voltageassisted perfusion method. ZFO nanocrystals were well anchored on the inner walls of the pristine TONTAs when the ZFO suspensions(0.025 mg m L^(-1)) were kept under a60 V bias voltage for 1 h. After annealing at 750 °C for2 h, the heterostructured ZFO/Fe_2 TiO_5(FTO)/TiO_2 composite nanotube arrays were successfully obtained. Furthermore, Fe^(3+)was reduced to Fe^(2+)when solid solution reactions occurred at the interface of ZFO and the pristine TONTAs. Introducing ZFO significantly enhanced thevisible light absorption of the ZFO/FTO/TONTAs relative to that of the annealed TONTAs. The coexistence of type I and staggered type II band alignment in the ZFO/FTO/TONTAs facilitated the separation of photogenerated electrons and holes, thereby improving the efficiency of the ZFO/FTO/TONTAs for photocatalytic degradation of methylene blue when irradiated with simulated sunlight.展开更多
基金financially supported by National Nature Science Foundation of China(Grant No.51402247 and 41630646)Sichuan Province Education Department Innovation Team Foundation(16zd1104)+2 种基金Sichuan Province Science Foundation for Young Scientists(No.15zs2111)Open Project of State Key Laboratory Cultivation Base for Nonmetal Composites and Functional Materials(No.13zxfk11)Doctoral Research Foundation of Southwest University of Science and Technology(No.14zx7119)
文摘To improve the visible light absorption and photocatalytic activity of titanium dioxide nanotube arrays(TONTAs), ZnFe_2O_4(ZFO) nanocrystals were perfused into pristine TONTA pipelines using a novel bias voltageassisted perfusion method. ZFO nanocrystals were well anchored on the inner walls of the pristine TONTAs when the ZFO suspensions(0.025 mg m L^(-1)) were kept under a60 V bias voltage for 1 h. After annealing at 750 °C for2 h, the heterostructured ZFO/Fe_2 TiO_5(FTO)/TiO_2 composite nanotube arrays were successfully obtained. Furthermore, Fe^(3+)was reduced to Fe^(2+)when solid solution reactions occurred at the interface of ZFO and the pristine TONTAs. Introducing ZFO significantly enhanced thevisible light absorption of the ZFO/FTO/TONTAs relative to that of the annealed TONTAs. The coexistence of type I and staggered type II band alignment in the ZFO/FTO/TONTAs facilitated the separation of photogenerated electrons and holes, thereby improving the efficiency of the ZFO/FTO/TONTAs for photocatalytic degradation of methylene blue when irradiated with simulated sunlight.