The corrosion and tribocorrosion behaviors of AISI 304 austenitic stainless steel and Cr26Mo1 ultrapure high chromium ferrite stainless steel in 3.5 wt.%NaCl and 0.5 mol/L H2SO4 solutions were investigated.Microelectr...The corrosion and tribocorrosion behaviors of AISI 304 austenitic stainless steel and Cr26Mo1 ultrapure high chromium ferrite stainless steel in 3.5 wt.%NaCl and 0.5 mol/L H2SO4 solutions were investigated.Microelectrode electrochemical measurement technology was applied to identify electrochemistry behaviors during tribocorrosion tests in situ.The surface morphologies and compositions of the wear tracks were analyzed by scanning electron microscopy and Raman spectrum.The results showed that compositions of stainless steels,corrosive mediums and applied loads have great influence on tribocorrosion behaviors of stainless steels.Firstly,the corrosion resistance in static state of stainless steels primarily dominates its tribocorrosion behavior;meanwhile,better mechanical properties are in favor of tribocorrosion resistance.Secondly,the corrosion rate is promoted significantly in 3.5%NaCl solution by friction,while the tendency is inconspicuous in 0.5 mol/L H2SO4 solution.Last but not least,passive films on stainless steels can be wiped off by small friction force.With the increase in applied load,the effect of friction converts to forming friction oxide film from removing passivation film,so that a critical load exists below which the friction force can promote the corrosion process extremely.展开更多
The γ/γ＇ microstructural evolution in a nickel based single crystal superalloy during load-free thermal exposure at 900 ℃ has been further investigated in this paper. The growth characteristics of γ＇ precipitate...The γ/γ＇ microstructural evolution in a nickel based single crystal superalloy during load-free thermal exposure at 900 ℃ has been further investigated in this paper. The growth characteristics of γ＇ precipitates were discussed in detail. The generation of interfacial dislocations would accelerate the rate of coalescence in the dendrite arms. The average sizes of precipitates were used to compare interface with diffusion controlled growth mechanism and no mechanism seems obviously dominant, although the square rate law gives slightly better fit. The coarsening behavior may be controlled by diffusion through the ragged interface between the γ＇ precipitate and the y matrix.展开更多
基金supported by PetroChina Key Core Technology Project(21ZG10)the Strategic Priority Research Program of the Chinese Academy of Sciences(Grant No.XDC04040400).
文摘The corrosion and tribocorrosion behaviors of AISI 304 austenitic stainless steel and Cr26Mo1 ultrapure high chromium ferrite stainless steel in 3.5 wt.%NaCl and 0.5 mol/L H2SO4 solutions were investigated.Microelectrode electrochemical measurement technology was applied to identify electrochemistry behaviors during tribocorrosion tests in situ.The surface morphologies and compositions of the wear tracks were analyzed by scanning electron microscopy and Raman spectrum.The results showed that compositions of stainless steels,corrosive mediums and applied loads have great influence on tribocorrosion behaviors of stainless steels.Firstly,the corrosion resistance in static state of stainless steels primarily dominates its tribocorrosion behavior;meanwhile,better mechanical properties are in favor of tribocorrosion resistance.Secondly,the corrosion rate is promoted significantly in 3.5%NaCl solution by friction,while the tendency is inconspicuous in 0.5 mol/L H2SO4 solution.Last but not least,passive films on stainless steels can be wiped off by small friction force.With the increase in applied load,the effect of friction converts to forming friction oxide film from removing passivation film,so that a critical load exists below which the friction force can promote the corrosion process extremely.
文摘The γ/γ＇ microstructural evolution in a nickel based single crystal superalloy during load-free thermal exposure at 900 ℃ has been further investigated in this paper. The growth characteristics of γ＇ precipitates were discussed in detail. The generation of interfacial dislocations would accelerate the rate of coalescence in the dendrite arms. The average sizes of precipitates were used to compare interface with diffusion controlled growth mechanism and no mechanism seems obviously dominant, although the square rate law gives slightly better fit. The coarsening behavior may be controlled by diffusion through the ragged interface between the γ＇ precipitate and the y matrix.