The long-term storage of phosphate tailings will occupy a large amount of land,pollute soil and groundwater,thus,it is crucial to achieve the harmless disposal of phosphate tailings.In this study,high-performance geop...The long-term storage of phosphate tailings will occupy a large amount of land,pollute soil and groundwater,thus,it is crucial to achieve the harmless disposal of phosphate tailings.In this study,high-performance geopolymers with compressive strength of 38.8 MPa were prepared by using phosphate tailings as the main raw material,fly ash as the active silicon-aluminum material,and water glass as the alkaline activator.The solid content of phosphate tailings and fly ash was 60% and 40%,respectively,and the water-cement ratio was 0.22.The results of XRD,FTIR,SEM-EDS and XPS show that the reactivity of phosphate tailings with alkaline activator is weak,and the silicon-aluminum material can react with alkaline activator to form zeolite and gel,and encapsulate/cover the phosphate tailings to form a dense phosphate tailings-based geopolymer.During the formation of geopolymers,part of the aluminum-oxygen tetrahedron replaced the silicon-oxygen tetrahedron,causing the polycondensation reaction between geopolymers and increasing the strength of geopolymers.The leaching toxicity test results show that the geopolymer has a good solid sealing effect on heavy metal ions.The preparation of geopolymer from phosphate tailings is an important way to alleviate the storage pressure and realize the resource utilization of phosphate tailings.展开更多
中子辐射俘获反应在反应堆运行、核装置设计及核天体物理研究中起重要的作用.4πBaF_(2)探测装置有着高时间分辨能力、低中子灵敏度、高探测效率等优点,适合开展中子辐射俘获反应截面数据的测量.中国原子能科学研究院核数据重点实验室...中子辐射俘获反应在反应堆运行、核装置设计及核天体物理研究中起重要的作用.4πBaF_(2)探测装置有着高时间分辨能力、低中子灵敏度、高探测效率等优点,适合开展中子辐射俘获反应截面数据的测量.中国原子能科学研究院核数据重点实验室建立了伽马全吸收装置(Gamma total absorption facility,GTAF),该装置用28块六棱BaF_(2)晶体和12块五棱BaF_(2)晶体构成了外径25 cm,内径10 cm的球壳,覆盖了95.2%的立体角.利用GTAF在中国散裂中子源Back-n束线上,测量了197Au(n,γ)的反应截面数据.测量数据通过能量筛选、PSD方法、晶体多重性筛选进行了初步本底扣除,随后结合对^(nat)C及空样品的测量数据对本底进行了分析及扣除,获得了197Au俘获反应的产额,利用SAMMY程序拟合得到了^(197)Au在1—100 e V的共振能量、中子共振宽度和伽马共振宽度参数.实验测量结果与ENDF/B-VIII.0数据库符合良好,其共振参数存在一定差异,分析原因可能与GTAF能量分辨率、Back-n的中子能谱测量精度、以及实验本底扣除方法相关,这也是下一步工作的重点.展开更多
基金Project(202202AG050010)supported by the Yunnan Major Scientific and Technological Projects,ChinaProject(202103AA080007)supported by the Key R&D Project of Science and Technology Department of Yunnan Province,ChinaProject(NECP2023-06)supported by the Open Project Fund of National Engineering and Technology Research Center for Development&Utilization of Phosphorous Resources,China。
文摘The long-term storage of phosphate tailings will occupy a large amount of land,pollute soil and groundwater,thus,it is crucial to achieve the harmless disposal of phosphate tailings.In this study,high-performance geopolymers with compressive strength of 38.8 MPa were prepared by using phosphate tailings as the main raw material,fly ash as the active silicon-aluminum material,and water glass as the alkaline activator.The solid content of phosphate tailings and fly ash was 60% and 40%,respectively,and the water-cement ratio was 0.22.The results of XRD,FTIR,SEM-EDS and XPS show that the reactivity of phosphate tailings with alkaline activator is weak,and the silicon-aluminum material can react with alkaline activator to form zeolite and gel,and encapsulate/cover the phosphate tailings to form a dense phosphate tailings-based geopolymer.During the formation of geopolymers,part of the aluminum-oxygen tetrahedron replaced the silicon-oxygen tetrahedron,causing the polycondensation reaction between geopolymers and increasing the strength of geopolymers.The leaching toxicity test results show that the geopolymer has a good solid sealing effect on heavy metal ions.The preparation of geopolymer from phosphate tailings is an important way to alleviate the storage pressure and realize the resource utilization of phosphate tailings.
文摘中子辐射俘获反应在反应堆运行、核装置设计及核天体物理研究中起重要的作用.4πBaF_(2)探测装置有着高时间分辨能力、低中子灵敏度、高探测效率等优点,适合开展中子辐射俘获反应截面数据的测量.中国原子能科学研究院核数据重点实验室建立了伽马全吸收装置(Gamma total absorption facility,GTAF),该装置用28块六棱BaF_(2)晶体和12块五棱BaF_(2)晶体构成了外径25 cm,内径10 cm的球壳,覆盖了95.2%的立体角.利用GTAF在中国散裂中子源Back-n束线上,测量了197Au(n,γ)的反应截面数据.测量数据通过能量筛选、PSD方法、晶体多重性筛选进行了初步本底扣除,随后结合对^(nat)C及空样品的测量数据对本底进行了分析及扣除,获得了197Au俘获反应的产额,利用SAMMY程序拟合得到了^(197)Au在1—100 e V的共振能量、中子共振宽度和伽马共振宽度参数.实验测量结果与ENDF/B-VIII.0数据库符合良好,其共振参数存在一定差异,分析原因可能与GTAF能量分辨率、Back-n的中子能谱测量精度、以及实验本底扣除方法相关,这也是下一步工作的重点.