Alumina-based composites containing 0-15wt% Ni metallic phase were produced by hot press-sintering Ni-coated alumina powders. The Ni-coated alumina powders were prepared by the aqueous heterogeneous precipitation of a...Alumina-based composites containing 0-15wt% Ni metallic phase were produced by hot press-sintering Ni-coated alumina powders. The Ni-coated alumina powders were prepared by the aqueous heterogeneous precipitation of alumina micro-powders and nickel sulfate salt followed by reduction process. The microstructural features and dispersion of Ni phase in Ni-coated alumina powders and the subsequent alumina-Ni cermets were investigated using scanning electron microscope （SEM）, X-ray diffractometer （XRD）, and transmission electron microscope （TEM）. The relative density of the hot press-sintered composites was measured with the Archimedes＇ method while the fracture strength and the fracture toughness were defined with the three-point bending method and the micro-indentation fracture method. In the formation of alumina-Ni cermets from sintered Ni-coated alumina powders, Ni phase to some extent limits the densification rate and stifles the coarsening and growing process of alumina grains. The Ni phase is found to be located at the interfaces and the triple-joint junctions of alumina grains which results into alteration of the fracture mode of alumina and its increased fracture strength and fracture toughness if compared with monolithic alumina.展开更多
基金Innovation Foundation of Jiangsu University(04CX01)
文摘Alumina-based composites containing 0-15wt% Ni metallic phase were produced by hot press-sintering Ni-coated alumina powders. The Ni-coated alumina powders were prepared by the aqueous heterogeneous precipitation of alumina micro-powders and nickel sulfate salt followed by reduction process. The microstructural features and dispersion of Ni phase in Ni-coated alumina powders and the subsequent alumina-Ni cermets were investigated using scanning electron microscope （SEM）, X-ray diffractometer （XRD）, and transmission electron microscope （TEM）. The relative density of the hot press-sintered composites was measured with the Archimedes＇ method while the fracture strength and the fracture toughness were defined with the three-point bending method and the micro-indentation fracture method. In the formation of alumina-Ni cermets from sintered Ni-coated alumina powders, Ni phase to some extent limits the densification rate and stifles the coarsening and growing process of alumina grains. The Ni phase is found to be located at the interfaces and the triple-joint junctions of alumina grains which results into alteration of the fracture mode of alumina and its increased fracture strength and fracture toughness if compared with monolithic alumina.