In this study,three kinds of dual-phase(DP) steels were used to investigate the influence of silicon content and intercritical annealing temperature on their microstructures,mechanical properties,and work-hardening be...In this study,three kinds of dual-phase(DP) steels were used to investigate the influence of silicon content and intercritical annealing temperature on their microstructures,mechanical properties,and work-hardening behaviors. By adding silicon and matching the critical annealing temperature,a new DP steel(1.0Si and intercritically annealed at 790 ℃) that exhibits an excellent combination of ultrahigh strength and adequate ductility was obtained. Variations in the strength,elongation,and fracture mechanism of the specimens with respect to different intercritical annealing temperatures were correlated to microstructural features. With an increase in the silicon content,there is no significant change in the martensitic band structure or ferrite morphology. At the same annealing temperature,the yield strength and yield strength ratio of the specimens decreased,but at different annealing temperatures,the tensile strength was reduced. The Hollomon analysis results indicate that the workhardening behavior obeys a two-stage work-hardening mechanism. With an increasing intercritical annealing temperature,the "transition strain"shifts to the left,and with an increasing silicon content,the "transition strain"shifts to the right. The surface exhibits ductile fractures characterized by a high density of microvoid dimples. With an increase in the silicon content,the average dimple size on the fracture surface decreases and the plasticity of the material increases.展开更多
文摘In this study,three kinds of dual-phase(DP) steels were used to investigate the influence of silicon content and intercritical annealing temperature on their microstructures,mechanical properties,and work-hardening behaviors. By adding silicon and matching the critical annealing temperature,a new DP steel(1.0Si and intercritically annealed at 790 ℃) that exhibits an excellent combination of ultrahigh strength and adequate ductility was obtained. Variations in the strength,elongation,and fracture mechanism of the specimens with respect to different intercritical annealing temperatures were correlated to microstructural features. With an increase in the silicon content,there is no significant change in the martensitic band structure or ferrite morphology. At the same annealing temperature,the yield strength and yield strength ratio of the specimens decreased,but at different annealing temperatures,the tensile strength was reduced. The Hollomon analysis results indicate that the workhardening behavior obeys a two-stage work-hardening mechanism. With an increasing intercritical annealing temperature,the "transition strain"shifts to the left,and with an increasing silicon content,the "transition strain"shifts to the right. The surface exhibits ductile fractures characterized by a high density of microvoid dimples. With an increase in the silicon content,the average dimple size on the fracture surface decreases and the plasticity of the material increases.