In this paper,15Cr-ODS steels containing 0,1 wt%,2 wt%and 3 wt%Al element were fabricated by combining wet-milling and spark plasma sintering(SPS)methods.The microstructure and mechanical properties of ODS steel were ...In this paper,15Cr-ODS steels containing 0,1 wt%,2 wt%and 3 wt%Al element were fabricated by combining wet-milling and spark plasma sintering(SPS)methods.The microstructure and mechanical properties of ODS steel were investigated by XRD,SEM,TEM,EBSD and tensile tests.The results demonstrate that the Al addition significantly refines the particle precipitates in the Fe-Cr matrix,leading to the obvious refinement in grain size of matrix and the improvement of mechanical properties.The dispersion particles in ODS steels with Al addition are identified as Al2O3 and Y_(2)Ti_(2)O_(7)nanoparticles,which has a heterogeneous size distribution in the range of 5 nm to 300 nm.Increasing Al addition causes an obvious increase in tensile strength and a decline in elongation.The tensile strength and elongation of 15Cr-ODS steel containing 3 wt%Al are 775.3 MPa and 15.1%,respectively.The existence of Al element improves the corrosion resistance of materials.The ODS steel containing 2 wt%Al shows corrosion potential of 0.39 V and passivation current density of 2.61×10^(−3)A/cm^(2)(1.37 V).This work shows that Al-doped ODS steels prepared by wet-milling and SPS methods have a potential application in structural parts for nuclear system.展开更多
基金Project(2020JJ2001)supported by Outstanding Youth Scientist Foundation of Hunan Province,ChinaProject(6142912200102)supported by Foundation for National Key Laboratory of Science and Technology on Highstrength Structural Materials,China。
文摘In this paper,15Cr-ODS steels containing 0,1 wt%,2 wt%and 3 wt%Al element were fabricated by combining wet-milling and spark plasma sintering(SPS)methods.The microstructure and mechanical properties of ODS steel were investigated by XRD,SEM,TEM,EBSD and tensile tests.The results demonstrate that the Al addition significantly refines the particle precipitates in the Fe-Cr matrix,leading to the obvious refinement in grain size of matrix and the improvement of mechanical properties.The dispersion particles in ODS steels with Al addition are identified as Al2O3 and Y_(2)Ti_(2)O_(7)nanoparticles,which has a heterogeneous size distribution in the range of 5 nm to 300 nm.Increasing Al addition causes an obvious increase in tensile strength and a decline in elongation.The tensile strength and elongation of 15Cr-ODS steel containing 3 wt%Al are 775.3 MPa and 15.1%,respectively.The existence of Al element improves the corrosion resistance of materials.The ODS steel containing 2 wt%Al shows corrosion potential of 0.39 V and passivation current density of 2.61×10^(−3)A/cm^(2)(1.37 V).This work shows that Al-doped ODS steels prepared by wet-milling and SPS methods have a potential application in structural parts for nuclear system.