Phase pure ZrB2-SiC composite powders were prepared after 1 450℃/3 h via carbothermal reduction route,by using ZrSiO4,B2O3 and carbon as the raw materials.The influences of firing temperature as well as the type and ...Phase pure ZrB2-SiC composite powders were prepared after 1 450℃/3 h via carbothermal reduction route,by using ZrSiO4,B2O3 and carbon as the raw materials.The influences of firing temperature as well as the type and amount of additive on the phase composition of final products were detailedly investigated.The results indicated that the onset formation temperature of ZrB2-SiC was reduced to 1 400℃by the present conditions,and oxide additive（including CoSO4·7H2O,Y2O3 and TiO2）was effective in enhancing the decomposition of raw ZrSiO4,therefore accelerating the synthesis of ZrB2-SiC.Moreover,microstructural observation showed that the as-prepared ZrB2 and SiC respectively had well-defined hexagonal columnar and fibrous morphology.Furthermore,the methodology of back-propagation artificial neural networks（BP-ANNs）was adopted to establish a model for predicting the reaction extent（e g,the content of ZrB2-SiC in final product）in terms of various processing conditions.The results predicted by the as-established BP-ANNs model matched well with that of testing experiment（with a mean square error in 10^（-3） degree）,verifying good effectiveness of the proposed strategy.展开更多
A rapid-heating method in the absence of electric/magnetic field was achieved by introducing a self-propagating-combustion （SHS） as heating source. The effect of heating rate on the alumina grain growth was explored...A rapid-heating method in the absence of electric/magnetic field was achieved by introducing a self-propagating-combustion （SHS） as heating source. The effect of heating rate on the alumina grain growth was explored based on this rapid-heating method. Comparing with the alumina prepared by two different heating ratios （greater than 1 000 ℃/min in SItS and about 50 ℃/min in common pressureless sintering furnace）, it was revealed that the rapid heating could promote the grain growth greatly without pressure during sintering. However, if a pressure was applied simultaneously, the grain growth would be almost completely restrained. Since these observations are quite different from the expectation, a new grain growth model was proposed.展开更多
基金Funded by National Natural Science Foundation of China(Nos.51502212,51672194 and 51472184)Hubei Province Natural Science Foundation of China(No.2018CFB760)+1 种基金Program for Innovative Teams of Outstanding Young and Middle-aged Researchers in the Higher Education Institutions of Hubei Province(No.T201602)Key Program of Natural Science Foundation of Hubei Province(No.2017CFA004)
文摘Phase pure ZrB2-SiC composite powders were prepared after 1 450℃/3 h via carbothermal reduction route,by using ZrSiO4,B2O3 and carbon as the raw materials.The influences of firing temperature as well as the type and amount of additive on the phase composition of final products were detailedly investigated.The results indicated that the onset formation temperature of ZrB2-SiC was reduced to 1 400℃by the present conditions,and oxide additive（including CoSO4·7H2O,Y2O3 and TiO2）was effective in enhancing the decomposition of raw ZrSiO4,therefore accelerating the synthesis of ZrB2-SiC.Moreover,microstructural observation showed that the as-prepared ZrB2 and SiC respectively had well-defined hexagonal columnar and fibrous morphology.Furthermore,the methodology of back-propagation artificial neural networks（BP-ANNs）was adopted to establish a model for predicting the reaction extent（e g,the content of ZrB2-SiC in final product）in terms of various processing conditions.The results predicted by the as-established BP-ANNs model matched well with that of testing experiment（with a mean square error in 10^（-3） degree）,verifying good effectiveness of the proposed strategy.
基金Funded by the National Natural Science Foundation of China(No.U12301013)the State Ministry of Science and Technology Innovation Fund(No.0102010DFA52240)
文摘A rapid-heating method in the absence of electric/magnetic field was achieved by introducing a self-propagating-combustion （SHS） as heating source. The effect of heating rate on the alumina grain growth was explored based on this rapid-heating method. Comparing with the alumina prepared by two different heating ratios （greater than 1 000 ℃/min in SItS and about 50 ℃/min in common pressureless sintering furnace）, it was revealed that the rapid heating could promote the grain growth greatly without pressure during sintering. However, if a pressure was applied simultaneously, the grain growth would be almost completely restrained. Since these observations are quite different from the expectation, a new grain growth model was proposed.