Based on the phase diagrams and the mass action law in combination with the coexistence theory of metallic melts structure, the calculation model of mass action concentration for Mg-Al, Sr-Al and Ba-Al was built, and ...Based on the phase diagrams and the mass action law in combination with the coexistence theory of metallic melts structure, the calculation model of mass action concentration for Mg-Al, Sr-Al and Ba-Al was built, and their thermodynamic parameters were determined. The agreement between calculated and measured results shows that the model and the determined thermodynamic parameters can reflect the structural characteristics of relevant melts. However, the fact that the thermodynamic parameters from literature don ′t give the value agree with the measured result may be due to unconformity of these parameters to real chemical reactions in metallic melts.展开更多
A new four-coordinated manganese compound Mn2（BPTC） （BPTC =- biphenyl- 2,4,4＇,6-tetracarboxylate） with flu topology net was synthesized under hydrothermal conditions. Single-crystal X-ray diffraction analysis con...A new four-coordinated manganese compound Mn2（BPTC） （BPTC =- biphenyl- 2,4,4＇,6-tetracarboxylate） with flu topology net was synthesized under hydrothermal conditions. Single-crystal X-ray diffraction analysis confirms its crystal belongs to the monoclinic system, space group C2/c with a = 12.2092（11）, b = 14.6932（9）, c = 8.9998（10） A, t= 108.256（12）°, Z= 4, V= 1533.2（2） A3, Dc = 1.889 mg/m3,μ = 1.69, F（O00） = 864, the final R = 0.063 and wR = 0.201 for 1407 observed reflections （I 〉 20（/））. UV-Vis absorption spectrum shows the title compound has a strong absorption at 326 and 238 nm and the optical diffuse reflectance determination shows the band gap of the title compound is 3.15 eV. The theory calculation elucidated that the UV absorptions of the title compound mainly arise from the electron transition from bonding orbitals of BPTC4- ligand to the empty orbitals of BPTC4- and Mn（II） ions.展开更多
The kinetics of voluminal reduction of chromium ore fines containing coal （COFCC） by microwave heating was studied. When the molar ratio of carbon to oxygen was 0.84 and that of CaO to SiO2 was 0.39 in COFCC, the te...The kinetics of voluminal reduction of chromium ore fines containing coal （COFCC） by microwave heating was studied. When the molar ratio of carbon to oxygen was 0.84 and that of CaO to SiO2 was 0.39 in COFCC, the temperature rising rate of COFCC by microwave heating was 62.5 ℃/min, 68.75 ℃/min, 70. 59 ℃/min, and 72.22 ℃/min at 1 000 ℃, 1 100 ℃, 1 200 ℃, and 1 300 ℃, respectively. The results show that the voluminal re duction of COFCC by microwave heating at solid-solid phase is first order reaction, with the apparent activation energy of 51. 480 kJ/mol. The limiting step of reaction rate for the overall reaction is the mass transfer of CO in the reduced product layer between dielectric particles of chromium ore and coal.展开更多
The solid-phase decarburization of high-carbon ferromanganese powders （HCFPs） was investigated using calcium carbonate as the decarburizer by microwave heating and conventional heating methods to explore the differ-...The solid-phase decarburization of high-carbon ferromanganese powders （HCFPs） was investigated using calcium carbonate as the decarburizer by microwave heating and conventional heating methods to explore the differ-ences of microwave heating and conventional heating. Experimental results show that HCFPs containing calcium.car-bonate were heated up to 900, 1000, 1 100, and 1200 ℃ and held for 60 rain for decarburization by microwave heat-ing at decarburization ratios of 76.69%, 82.90%, 84.11%, and 85. 75%, respectively. These ratios are higher than the decarburization ratios used for conventional heating under the same experimental conditipns. The microwave heat- ing can significantly improve decarburization ratio. This indicates the microwave heating field features a non-thermal effect, which in turn, visibly enhances the carbon diffusion ability of HCFPs. It also improves the kinetic conditions of solid-phase decarburization.展开更多
To avoid the nonuniform phenomena of heat and mass transfer of metallurgical powdery materials caused by conventional heating method,the temperature rise characteristics of carbon-containing chromite ore fines in the ...To avoid the nonuniform phenomena of heat and mass transfer of metallurgical powdery materials caused by conventional heating method,the temperature rise characteristics of carbon-containing chromite ore fines in the microwave field were investigated using microwave heating in a microwave metallurgical furnace.The experimental results show that the carbon-containing chromite ore fines have better temperature rise characteristics in the microwave field at a frequency of 2.45 GHz.After heated in the microwave field of 10 kW,the temperature of 1 kg carbon-containing chromite ore fines rose up to 1 100 ℃ in 7 min,at a temperature rise rate of 157.1（℃·min-1·kg-1）,whereas the temperature of 1 kg carbon-containing magnetite ore fines rose only up to 1 000 ℃ in 10 min,at a temperature rise rate of 100（℃·min-1·kg-1）.With increasing carbon-fitting ratios and by adding calcic lime,their heating effects changed regularly.展开更多
文摘Based on the phase diagrams and the mass action law in combination with the coexistence theory of metallic melts structure, the calculation model of mass action concentration for Mg-Al, Sr-Al and Ba-Al was built, and their thermodynamic parameters were determined. The agreement between calculated and measured results shows that the model and the determined thermodynamic parameters can reflect the structural characteristics of relevant melts. However, the fact that the thermodynamic parameters from literature don ′t give the value agree with the measured result may be due to unconformity of these parameters to real chemical reactions in metallic melts.
基金supported by the Natural Science Foundation of Fujian Province(No.2014J01029)the National Natural Science Foundation of China(No.91122028)
文摘A new four-coordinated manganese compound Mn2（BPTC） （BPTC =- biphenyl- 2,4,4＇,6-tetracarboxylate） with flu topology net was synthesized under hydrothermal conditions. Single-crystal X-ray diffraction analysis confirms its crystal belongs to the monoclinic system, space group C2/c with a = 12.2092（11）, b = 14.6932（9）, c = 8.9998（10） A, t= 108.256（12）°, Z= 4, V= 1533.2（2） A3, Dc = 1.889 mg/m3,μ = 1.69, F（O00） = 864, the final R = 0.063 and wR = 0.201 for 1407 observed reflections （I 〉 20（/））. UV-Vis absorption spectrum shows the title compound has a strong absorption at 326 and 238 nm and the optical diffuse reflectance determination shows the band gap of the title compound is 3.15 eV. The theory calculation elucidated that the UV absorptions of the title compound mainly arise from the electron transition from bonding orbitals of BPTC4- ligand to the empty orbitals of BPTC4- and Mn（II） ions.
基金Item Sponsored by National Natural Science Foundation of China and Baoshan Iron and Steel Co Ltd of China(50474083)
文摘The kinetics of voluminal reduction of chromium ore fines containing coal （COFCC） by microwave heating was studied. When the molar ratio of carbon to oxygen was 0.84 and that of CaO to SiO2 was 0.39 in COFCC, the temperature rising rate of COFCC by microwave heating was 62.5 ℃/min, 68.75 ℃/min, 70. 59 ℃/min, and 72.22 ℃/min at 1 000 ℃, 1 100 ℃, 1 200 ℃, and 1 300 ℃, respectively. The results show that the voluminal re duction of COFCC by microwave heating at solid-solid phase is first order reaction, with the apparent activation energy of 51. 480 kJ/mol. The limiting step of reaction rate for the overall reaction is the mass transfer of CO in the reduced product layer between dielectric particles of chromium ore and coal.
基金Item Sponsored by National Natural Science Foundation of China and Baosteel Group Corporation of China(50974149)
文摘The solid-phase decarburization of high-carbon ferromanganese powders （HCFPs） was investigated using calcium carbonate as the decarburizer by microwave heating and conventional heating methods to explore the differ-ences of microwave heating and conventional heating. Experimental results show that HCFPs containing calcium.car-bonate were heated up to 900, 1000, 1 100, and 1200 ℃ and held for 60 rain for decarburization by microwave heat-ing at decarburization ratios of 76.69%, 82.90%, 84.11%, and 85. 75%, respectively. These ratios are higher than the decarburization ratios used for conventional heating under the same experimental conditipns. The microwave heat- ing can significantly improve decarburization ratio. This indicates the microwave heating field features a non-thermal effect, which in turn, visibly enhances the carbon diffusion ability of HCFPs. It also improves the kinetic conditions of solid-phase decarburization.
基金Item Sponsored by National Natural Science Foundation of China and Baoshan Iron and Steel Group Co(50474083)
文摘To avoid the nonuniform phenomena of heat and mass transfer of metallurgical powdery materials caused by conventional heating method,the temperature rise characteristics of carbon-containing chromite ore fines in the microwave field were investigated using microwave heating in a microwave metallurgical furnace.The experimental results show that the carbon-containing chromite ore fines have better temperature rise characteristics in the microwave field at a frequency of 2.45 GHz.After heated in the microwave field of 10 kW,the temperature of 1 kg carbon-containing chromite ore fines rose up to 1 100 ℃ in 7 min,at a temperature rise rate of 157.1（℃·min-1·kg-1）,whereas the temperature of 1 kg carbon-containing magnetite ore fines rose only up to 1 000 ℃ in 10 min,at a temperature rise rate of 100（℃·min-1·kg-1）.With increasing carbon-fitting ratios and by adding calcic lime,their heating effects changed regularly.