Nano-silver and waterborne polyurethane(WPU)composite emulsion was synthesized.The average diameter of silver nanoparticles(SNPs)was about 20 nm,and the average diameter of WPU was 101.32 nm.The anti-bacteria finishin...Nano-silver and waterborne polyurethane(WPU)composite emulsion was synthesized.The average diameter of silver nanoparticles(SNPs)was about 20 nm,and the average diameter of WPU was 101.32 nm.The anti-bacteria finishing of a polypropylene non-woven fabric(NWF)was carried out by ultraviolet finishing technology and the double dipping twin-roll method.The standard AATCC100 was used to test the antimicrobial activity of the samples.The results showed that the antimicrobial rates of Klebsiella pneumoniae(K.pneumoniae)and Staphylococcus aureus(S.aureus)were above 90%,which indicated that the NWF finishing had good antimicrobial activity.In addition,the thermal stability,mechanical properties,whiteness and contact angle of antimicrobial finishing nonwovens were characterized.The results showed that the performance of antimicrobial nonwovens was stable at 300℃.The breaking strength was better than that of untreated nonwovens,and the contact angle reached 119.1°.展开更多
基金National Natural Science Foundation of China(Regional Fund)(No.51863020)
文摘Nano-silver and waterborne polyurethane(WPU)composite emulsion was synthesized.The average diameter of silver nanoparticles(SNPs)was about 20 nm,and the average diameter of WPU was 101.32 nm.The anti-bacteria finishing of a polypropylene non-woven fabric(NWF)was carried out by ultraviolet finishing technology and the double dipping twin-roll method.The standard AATCC100 was used to test the antimicrobial activity of the samples.The results showed that the antimicrobial rates of Klebsiella pneumoniae(K.pneumoniae)and Staphylococcus aureus(S.aureus)were above 90%,which indicated that the NWF finishing had good antimicrobial activity.In addition,the thermal stability,mechanical properties,whiteness and contact angle of antimicrobial finishing nonwovens were characterized.The results showed that the performance of antimicrobial nonwovens was stable at 300℃.The breaking strength was better than that of untreated nonwovens,and the contact angle reached 119.1°.