An intrinsic sensor(diameter 16 mm,thickness 300 μm) based on chemical vapor deposition derived polycrystalline diamond was developed.Ultra low dark current under 100 pA and high n/discrimination of 15.8 were obtaine...An intrinsic sensor(diameter 16 mm,thickness 300 μm) based on chemical vapor deposition derived polycrystalline diamond was developed.Ultra low dark current under 100 pA and high n/discrimination of 15.8 were obtained on this device,which enable it to be used for neutron detection in multi-radiation field.Moreover,the neutron sensitivity of this detector was characterized theoretically and experimentally.And for fast and ultra-fast neutron,the detection sensitivity is in the magnitude of 10 17 to 10 16 C cm 2 /n with good stability and negligible pump effect.All these results indicate that the as-prepared sensor to be ideal for fast and ultra-fast neutron monitoring,and it may pave the way to build neutron detector with low cost and large sensitive area with diamond.展开更多
基金supported by the National Natural Science Foundation of China (Grant Nos. 11175142,11175141 and 11105106)the National Hi-Tech Project of China (Grant No. 2009AA050705)the State Key Laboratory of Multiphase Flow (Xi’an Jiaotong University)
文摘An intrinsic sensor(diameter 16 mm,thickness 300 μm) based on chemical vapor deposition derived polycrystalline diamond was developed.Ultra low dark current under 100 pA and high n/discrimination of 15.8 were obtained on this device,which enable it to be used for neutron detection in multi-radiation field.Moreover,the neutron sensitivity of this detector was characterized theoretically and experimentally.And for fast and ultra-fast neutron,the detection sensitivity is in the magnitude of 10 17 to 10 16 C cm 2 /n with good stability and negligible pump effect.All these results indicate that the as-prepared sensor to be ideal for fast and ultra-fast neutron monitoring,and it may pave the way to build neutron detector with low cost and large sensitive area with diamond.