独居石是典型伴生铀、钍的稀土矿资源,通过现有的碱溶转化、优溶等步骤提取稀土后,所得优溶渣是富含铀、钍、稀土的重要二次资源。为与稀土提取保持一致的盐酸体系,研究优溶渣的盐酸浸出过程对整体回收工艺十分关键。采取单因素试验考察浸出过程条件对铀、钍、稀土浸出率的影响。结果表明,使用下述优化参数:盐酸浓度6 mol/L、浸出时间1.5~2 h、浸出温度60℃、液固体积质量比3 mL/g时,优溶渣中铀、钍、稀土的浸出率分别可达90%~95%、92%~93%、>60%,实现了较高的资源回收率。浸出渣的工艺矿物学分析表明,其主要由锆石、钍化合物和石英等脉石矿物组成。剩余的稀土组分则主要集中在未分解的独居石中,其余为少量磷钇矿和褐钇铌矿。试验结果可为独居石优溶渣的综合回收技术提供基础数据和支撑。

变频供电对异步电机电磁噪声的影响

针对某三相异步电机变频供电时,电机噪声明显增大且出现刺耳高频声的情况,利用数值仿真软件建立了电机磁场、振动和噪声模型,计算和分析了变频供电对电机定子电流、径向电磁力、电机振动和噪声的影响。研究发现,变频器供电时,电机定子电流在基波之外增加了基波的谐波分量和载波与谐波相互作用的频率分量,载波引起的电流分量增加了电磁力波的高阶分量,在研究频率范围内(个别频率除外),相比于正弦供电,电机振动速度增大至1.08~131.4倍,声压级增大了2.6~42.6dB。

用N503从低浓度铌溶液中萃取铌试验研究

研究了用N503从低浓度铌溶液中萃取铌,再用水反萃取载铌有机相,制备五氧化二铌,确定了最佳萃取及反萃取条件。结果表明:控制含铌溶液中氢氟酸浓度2.5 mol/L、硫酸浓度2 mol/L,在萃取剂为25%N503+75%磺化煤油、萃取时间3 min、萃取相比V_(o)/V_(a)=1/1.5条件下进行5级逆流萃取,铌萃取率大于90%;在反萃取相比V_(o)/V_(a)=3/1、反萃取时间7 min、反萃取温度30℃条件下,用水单级反萃取载铌有机相,铌反萃取率大于95%。用N503萃取—水反萃取低浓度铌溶液可制得纯度大于95%的五氧化二铌产品。

高超声速火星进入环境中颗粒运动特性研究

火星大气中会发生不同规模的沙尘暴,大气中蕴含的尘埃颗粒会对高速进入的火星探测器表面造成侵蚀并导致壁面热流增加,给探测器的热防护系统设计带来巨大挑战.文章针对高超声速火星进入环境两相流动问题,基于Euler-Lagrange框架建立非平衡流场与颗粒的单向耦合计算方法,采用模态半径为0.35μm的火星大气颗粒分布模型,研究不同尺寸颗粒在流场中的运动轨迹,获得高温相变模型对颗粒运动的影响以及不同粒径颗粒的撞击能量分布.结果表明,颗粒在高温流场中运动会吸热融化甚至蒸发,高温相变模型导致的颗粒直径减小对小尺寸颗粒运动轨迹有较大影响;当前计算状态下,直径3μm以上的颗粒具有较大的Stokes数且颗粒半径在运动过程中基本保持不变,其运动轨迹受流场影响较小,该尺寸颗粒的撞击分数均达95%以上,是造成壁面撞击的主要颗粒尺寸;撞击能量分数结果表明,直径3~10μm之间的颗粒是撞击能量的主要来源,约占总撞击能量的80%.

用N235从独居石优溶渣浸出液中萃取铁的动力学研究

采用恒界面池法研究了N235从独居石优溶渣浸出液中萃取铁的萃取动力学,在室温下考察了搅拌速度、比界面积、N235体积分数、改性剂仲辛醇体积分数、初始铁质量浓度和盐酸浓度对铁的正向萃取速率的影响。结果表明:搅拌速度小于90 r/min时,萃取过程由扩散反应控制,铁的萃取速率随搅拌速度增大而增大;搅拌速度大于90 r/min后,萃取速率不再变化,萃取过程为化学反应控制;随比界面积增加,萃取速率加快,萃取过程受界面混合控制;增大铁、盐酸和N235用量可加快萃取速率,增大仲辛醇用量可减缓萃取速率。在室温条件下,独居石优溶渣浸出液中铁的萃取动力学方程为:R 0=0.037[Fe]0.94[HCl]0.72[N235]0.52。

OS-X0试验飞行器声爆特性飞行测量与数值模拟分析

声爆问题是目前制约超声速民机研制的核心关键问题。但是,目前国内外关于声爆的飞行试验测试数据非常匮乏,严重制约了声爆预测与低声爆技术发展。基于零壹空间公司的"重庆两江之星"号OS-X0科学试验飞行器,航空工业气动院进行了声爆的飞行试验研究。采用航空工业气动院研发的飞行过程声爆信号地面测量技术成功获得了OS-X0试验飞行器在真实大气环境下的地面声爆信号,借助ARI_Boom声爆数值模拟平台对数据进行了分析和整理。数值计算结果与真实试验测量结果总体符合较好,但仍存在一定差异,这表明真实飞行环境下影响声爆特征的因素较多,在超声速飞行器声爆理论和预测方法等方面还需更深入的研究,同时飞行试验测量技术也有待进一步提高。

用硫酸/氢氟酸从铌钛铀矿石中协同浸出铀铌

研究了采用硫酸/氢氟酸从铌钛铀矿石中协同浸出铀、铌,考察了硫酸用量、氢氟酸用量、浸出温度、浸出时间、液固体积质量比对铀、铌浸出率的影响。试验结果表明:在硫酸用量150 g/kg、氢氟酸用量100 g/kg、液固体积质量比1.2 mL/g、浸出温度90℃、浸出时间2 h优化条件下,铀、铌浸出率分别为97%、85%,实现了铀、铌的同步高效浸出。

有色金属提取冶金技术现状及发展趋势分析

有色金属提取冶金技术主要包括增值冶金、金属加工、电冶金、湿法冶金和火法冶金。本文在此基础上,首先针对有色金属提取冶金技术的现状进行分析,在这个基础上就有色金属提取冶金技术的发展趋势进行预测。

某泥岩型铀矿石预处理技术研究

我国北方某泥岩型铀矿石泥化严重,矿石中的碳酸盐矿物和石膏含量高,采用常规搅拌直接浸出回收铀时,试剂消耗量大、铀浸出率低、生产成本高。为解决此问题,在浸出之前先对矿石进行了搅拌打散—筛分分级—粗粒堆浸—细粒浮选分组预处理,即将矿石分成+0.15 mm和-0.15mm两个粒级,80%以上的石膏赋存于+0.15 mm粗粒级中,这部分矿石可以不磨矿,采用堆浸法能够回收其中的铀,铀浸出率87.50%;90%以上的碳酸盐矿物赋存于-0.15 mm细粒级中,该粒级以氧化石蜡皂作为碳酸盐矿物浮选的捕收剂,水玻璃作为分散剂和活化剂,采用1次粗选2次精选开路浮选工艺流程处理,可获得-0.15 mm粒级高碳酸盐含铀产品和低碳酸盐含铀产品,高碳酸盐含铀产品作业产率28.72%,CO2含量33.85%,作业回收率84.68%。

声爆近场压力测量风洞试验技术研究进展

声爆是超声速民用飞机研制的关键问题之一,风洞试验作为开展声爆研究必不可少的技术手段具有重要研究意义。简要介绍了声爆风洞试验的特点与难点,分析了声爆风洞试验技术的发展趋势。按照空间压力测量装置的不同,将试验技术归纳为测压板、静压探针、测压轨、无反射测压轨等四类空间压力测量技术。重点针对基于无反射测压轨的空间压力精确测量技术和数据修正技术进行了总结与分析。无反射测压轨具有试验效率高、测量精度高、可有效降低流场非均匀扰动误差等优点,是声爆近场压力测量技术的重要发展方向。

用N235从某铀矿石酸性浸出液中萃取铀试验研究

研究了用N235从某铀矿石浸出液中溶剂萃取铀,考察了萃原液pH、温度、接触时间、相比等因素对萃取、反萃取的影响。通过5级逆流萃取、2级洗涤、4级逆流反萃取,铀萃取率98.5%,铀反萃取率98.9%。

A Method for Calculating Bottom Backscattering Strength Using Omnidirectional Projector and Omnidirectional Hydrophone

A method of obtaining bottom backscattering strength by employing an omnidirectional projector and omnidirectional hydrophone is proposed. The backscattering strength is extracted from monostatic backscattering data. The method was adopted in an experiment conducted in the South Yellow Sea of China. The seafloor surface was relatively smooth and covered by a small quantity of shell fragments, as observed through a digital camera system. Sampling data showed that the main component of the sediment at this experimental site was fine sand. In this paper, we detail the calculation method. Preliminary results of backscattering strength as a function of grazing angle(20?–70?) in the frequency range of 6–24 kHz are presented. The measured backscattering strength increased with the grazing angle and changed more rapidly at large grazing angles(60?–70?). A comparison of the data at different frequencies reveals that the measured backscattering strength substantially rises with the increase of acoustic frequency. A fitting curve of Lambert's law against the measured data shows that the backscattering strength deviates from Lambert's law at large grazing angles.

电加热器故障在线监测系统开发

针对传统的恒温恒湿设备电加热器出现故障时无法自动判断原因,设备结构复杂,拆装不便,严重影响汽车发动机试验开发效率等问题,自主开发设计了电加热器故障在线监测系统,该系统对工作中的电加热器电流进行监测,实时分析电加热器的工作状态。电加热器工作时,系统对电加热器的电流进行监测,当电流波动范围超出允许范围时,系统报警提示,电加热器显示故障。

组合式宽马赫数风洞设计与流场特性

脉冲型风洞是开展高超声速飞行器研制和气动热力学研究的重要试验设备。本文基于激波风洞和Ludwieg管风洞组合运行原理,突破了高温管外静态加热技术、高温高压气体隔离技术、大口径高温膜片设计技术等系列关键技术,设计建设了FL-63脉冲型组合式宽马赫数风洞,设计马赫数范围3.0~10.0,采用双模式组合运行模式,中低马赫数段(Ma 3.0~4.5)采用Ludwieg管风洞运行模式,最高温度可达900K,可复现飞行高度的总焓和总压,有效运行时间大于150ms;高马赫数段(Ma5.0~10.0)采用激波风洞运行模式,有效运行时间大于20ms,最高驱动压力30MPa。本文通过运行方式的灵活组合,兼顾了低马赫数和高马赫数来流的不同模拟需求,实现了宽马赫数范围的试验能力。

透明质酸钠凝胶预防术后肠粘连的随机对照研究

目的评价透明质酸钠凝胶对预防性肠造口术后预防粘连的有效性和安全性。方法采用前瞻性、多中心、随机和对照的方法,将来自6家医院的124例接受预防性肠造口术患者随机分配至透明质酸钠凝胶治疗组(59例)和空白对照组(65例)。比较两组在造口还纳手术时造口区域切口周围中、重度粘连发生率和安全性。结果研究组造口区域切口周围中、重度粘连发生率为6.3%,空白对照组为32.6%,研究组和空白对照组相比差异有统计学意义(P<0.05)。结论透明质酸钠凝胶可安全有效地减少术后中、重度肠粘连发生率。

基于概率模型的声爆试验数据分析

声爆是研制超声速民用飞机所需解决的关键问题之一,风洞试验是开展声爆研究的重要方式。简要介绍了进行声爆试验的方法与困难及相应的应对措施,以及超声速风洞声爆试验模型近场空间压力精确测量技术。重点针对国际上通常采用的精确测量数据修正技术:参考车次方法及空间平均方法,分析其原理及不足。提出概率模型方法对声爆试验进行数据分析,将复杂的风洞环境中各种不确定因素所造成的干扰参数化,用概率模型表达其不确定性。概率模型方法无需进行参考车次试验,用更少的数据得到更为准确的结果,并在与传统方法结果对比中表现出了该方法的合理性及可行性。

发动机喷管羽流对近场声爆特性影响的风洞试验技术

超声速飞行所引发的声爆问题是困扰新一代环保型超声速客机发展的关键技术难题,发动机喷管羽流对全机声爆特性尤其是后激波特性具有重要影响。设计了单喷管喷流试验模型及声爆试验装置,评估了风洞试验段洞壁反射激波对模型近场压力测量的影响,重点针对通气支臂对喷管羽流的支撑干扰问题进行了分析与优化。基于中国航空工业空气动力研究院FL-60风洞,开展了发动机喷管羽流对旋成体单喷管模型近场声爆特性影响试验技术研究,试验来流马赫数2.0、落压比(NPR)范围1~20.39。研究结果表明,通过对来流马赫数、通气支臂外形、喷流模型长度、通气支臂与模型的相对位置等参数的综合优化,消除了通气支臂带来的支撑干扰对喷管羽流的影响,确保在风洞试验段受限空间内模型近场压力测量不受洞壁反射和通气支臂波系的影响;喷管羽流主要对模型尾部的近场压力特征产生影响,在来流马赫数一定的条件下,提高喷管NPR使喷流状态从过膨胀到欠膨胀,喷管唇口激波逐渐增强、位置逐渐向上游移动,抑制了喷管船尾膨胀波的发展。

某独居石优溶渣二段逆流浸出试验研究

针对某独居石优溶渣,研究了采用一段常规浸出—二段逆流浸出工艺浸出铀、钍、稀土。考察了各因素对浸出效果的影响。结果表明:采用一段常规浸出法时,适宜条件下的铀、钍、稀土浸出率分别为98.66%、95.37%、64.23%;采用二段逆流浸出法时,铀、钍、稀土浸出率均可提高0.5%~1.0%,浸出液余酸降低50%以上,矿浆固液分离性能得到了一定改善。

钠化焙烧法从SCR废脱硝催化剂中回收钛

采用钠化焙烧法从废SCR脱硝催化剂中回收钛,研究了碱用量、焙烧温度、时间、物料粒度、不同硫酸浓度等因素对钛提取率的影响。根据试验结果确定了最佳的焙烧反应条件为:碱用量为理论用量的1.2倍,焙烧温度700℃,焙烧时间3 h,物料粒度-150μm。焙烧熟料水洗后采用质量浓度为45%的硫酸浸出,钛浸出率大于89%。浸出液经常压水解制备二氧化钛,钛沉淀率大于93%,二氧化钛产品纯度大于93%。