The effects of gas, pressure and temperature on the production of amorphous carbon nanotubes were inves- tigated using an arc discharging furnace at controlled tem- perature. Co/Ni alloy powder was used as catalyst. T...The effects of gas, pressure and temperature on the production of amorphous carbon nanotubes were inves- tigated using an arc discharging furnace at controlled tem- perature. Co/Ni alloy powder was used as catalyst. The dis- charge current was 80 A and voltage was 32 V. The optimal parameters were obtained: 600℃ temperature, hydrogen gas and 500 torr pressure. The productivity and purity of amorphous carbon nanotubes are 6.5 gram per hour and 80%, respectively. The diameter of the amorphous carbon nanotubes is about 7—20 nm.展开更多
文摘The effects of gas, pressure and temperature on the production of amorphous carbon nanotubes were inves- tigated using an arc discharging furnace at controlled tem- perature. Co/Ni alloy powder was used as catalyst. The dis- charge current was 80 A and voltage was 32 V. The optimal parameters were obtained: 600℃ temperature, hydrogen gas and 500 torr pressure. The productivity and purity of amorphous carbon nanotubes are 6.5 gram per hour and 80%, respectively. The diameter of the amorphous carbon nanotubes is about 7—20 nm.