The waste coffee-grounds carbon(WCGC)was prepared with H_(3)PO_(4)treated using waste coffee-grounds as precursor.Its adsorption ability was studied using phenol as test molecule.The influence of H_(3)PO_(4)treated,ca...The waste coffee-grounds carbon(WCGC)was prepared with H_(3)PO_(4)treated using waste coffee-grounds as precursor.Its adsorption ability was studied using phenol as test molecule.The influence of H_(3)PO_(4)treated,calcined temperature,the initial phenol concentration,the doge of carbon and original pH values on phenol adsorption ability were investigated.Characterization of WCGC was performed by N_(2)adsorption isotherms,Fourier transform infrared spectroscopy(FT-IR),scanning electron microscopy(SEM),and X-ray diffraction(XRD)techniques.First,the second order and Weber-Morris model reaction rate models were used to estimate the WCGC adsorption ability.The results show that the produced WCGC(700℃,2 h)has been graphitized and the layered structure increased BET surface to 435.98 m^(2)/g and adsorption phenol ability.The initial phenol concentration is 50 mg/L,the amount of WCGC(700℃,2 h)is 0.2 g,and the phenol adsorption rate is 97%after 270 min and no intermediate product formation.The adsorption kinetics of the selected WCGC is best fitted by the Weber-Morris model.展开更多
基金Funded by Yunnan Provincial Agricultural Joint Project(No.2018FG001-051)Yunnan Provincial Department of Education Research Fund(No.2020Y0414)
文摘The waste coffee-grounds carbon(WCGC)was prepared with H_(3)PO_(4)treated using waste coffee-grounds as precursor.Its adsorption ability was studied using phenol as test molecule.The influence of H_(3)PO_(4)treated,calcined temperature,the initial phenol concentration,the doge of carbon and original pH values on phenol adsorption ability were investigated.Characterization of WCGC was performed by N_(2)adsorption isotherms,Fourier transform infrared spectroscopy(FT-IR),scanning electron microscopy(SEM),and X-ray diffraction(XRD)techniques.First,the second order and Weber-Morris model reaction rate models were used to estimate the WCGC adsorption ability.The results show that the produced WCGC(700℃,2 h)has been graphitized and the layered structure increased BET surface to 435.98 m^(2)/g and adsorption phenol ability.The initial phenol concentration is 50 mg/L,the amount of WCGC(700℃,2 h)is 0.2 g,and the phenol adsorption rate is 97%after 270 min and no intermediate product formation.The adsorption kinetics of the selected WCGC is best fitted by the Weber-Morris model.